Iupilon® GSH2030R2
| Category: | PC , Polycarbonate |
| Manufacturer: | Mitsubishi Engineering-Plastics Corp |
| Trademark: | Iupilon® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | CP2FdY_Iupilon-GSH2030R2.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Iupilon® GSH2030R2 is a Polycarbonate (PC) material filled with 30% glass fiber. It is available in Asia Pacific, Europe, or North America for injection molding. Primary attribute of Iupilon® GSH2030R2: Flame Rated. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.43 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (300°C/1.2 kg) | 5.7 | g/10 min | ISO 1133 |
| Melt Volume-Flow Rate (MVR) (300°C/1.2 kg) | 4.80 | cm³/10min | ISO 1133 |
| Molding Shrinkage | |||
| Across Flow : 3.20 mm | 0.25 to 0.45 | % | |
| Flow : 3.20 mm | 0.050 to 0.25 | % | |
| Water Absorption (Saturation, 23°C) | 0.090 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 8900 | MPa | ISO 527-2 |
| Tensile Stress (Break) | 120 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 2.5 | % | ISO 527-2 |
| Flexural Modulus | 8500 | MPa | ISO 178 |
| Flexural Stress | 180 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 15 | kJ/m² | ISO 179 |
| Charpy Unnotched Impact Strength (23°C) | 50 | kJ/m² | ISO 179 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 148 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 144 | °C | ISO 75-2/A |
| CLTE | ISO 11359-2 | ||
| Flow | 1.8E-5 | cm/cm/°C | |
| Transverse | 6.3E-5 | cm/cm/°C |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 2.0E+15 | ohms | IEC 60093 |
| Volume Resistivity | 2.0E+16 | ohms·cm | IEC 60093 |
| Electric Strength | IEC 60243-1 | ||
| 1.00 mm | 32 | kV/mm | |
| 3.00 mm | 20 | kV/mm | |
| Relative Permittivity | IEC 60250 | ||
| 100 Hz | 3.60 | ||
| 1 MHz | 3.50 | ||
| Dissipation Factor | IEC 60250 | ||
| 100 Hz | 1.1E-3 | ||
| 1 MHz | 8.4E-3 | ||
| Comparative Tracking Index (CTI) | PLC 4 | UL 746 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (0.400 mm) | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Rear Temperature | 270 to 290 | °C | |
| Middle Temperature | 280 to 300 | °C | |
| Front Temperature | 290 to 310 | °C | |
| Nozzle Temperature | 290 to 310 | °C | |
| Mold Temperature | 80.0 to 120 | °C | |
| Injection Pressure | 50.0 to 150 | MPa | |
| Screw Speed | 50 to 100 | rpm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TAROLOX 10 K6 | Taro Plast S.p.A. | PBT | TAROLOX |
| Elastron® G G400.A40.N | Elastron USA, Inc. | SEBS | Elastron® G |
| Karina COMP. PVC CRYSTAL -E 70/264 | Karina Ind. e Com. de Plásticos Ltda | PVC, Flexible | Karina |
| MACOMASS PVC MM-PVC E 1580 | MACOMASS Verkaufs AG | PVC, Flexible | MACOMASS PVC |
| Jam 38504 UV | Jam Petrochemical Company | LMDPE | Jam |