| Category: | PP Impact Copolymer , Polypropylene Impact Copolymer |
| Manufacturer: | Southland Polymers |
| Trademark: | Pro-Comp™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | COeDYc_Pro-Comp-PPBGF40-E.pdf |
| PRICE: | Order Products email sales@su-jiao.com |
| Message |
|---|
| Procomp Enhanced Impact grades of glass filled polyproylene are specifically formulated to provide high stiffness while also offering good impact resistance. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.21 | g/cm³ | ASTM D792 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | 74.5 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 4.0 | % | ASTM D638 |
| Flexural Modulus | 3590 | MPa | ASTM D790 |
| Flexural Strength | 82.7 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | 180 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed | 152 | °C | |
| 1.8 MPa, Unannealed | 127 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Thermec™ 4150CF50 | Technical Polymers, LLC | PPS | Thermec™ |
| WELLAMID Nylon 6000 GVS 20/10 HWCP | CP-Polymer-Technik GmbH & Co. KG | Nylon 6 | WELLAMID Nylon |
| Braskem PE GM 5010 T2 B | Braskem | HDPE | Braskem PE |
| DynaMix™ 2044-GBID | Polymer Dynamix | Nylon, Unspecified | DynaMix™ |
| Hanwha Total PP TB52 | HANWHA TOTAL PETROCHEMICALS Co., Ltd. | PP, High Crystal | Hanwha Total PP |