GLS Acetal UN02
| Category: | Acetal (POM) Copolymer , Acetal (POM) Copolymer |
| Manufacturer: | GLS Polymers Pvt. Ltd. |
| Trademark: | GLS Acetal |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | CNvPEi_GLS-Acetal-UN02.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| POM UV RED |
| General Information | |
|---|---|
| Features |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.40 to 1.42 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | > 10 | g/10 min | ASTM D1238 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1(Yield) | 60.0 to 68.0 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 12 to 18 | % | ASTM D638 |
| Flexural Modulus | 2700 to 3100 | MPa | ASTM D790 |
| Flexural Strength 2 | 88.0 to 100 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (3.20 mm) | 90 to 110 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 112 to 116 | °C | ASTM D648 |
| Vicat Softening Temperature | 165 to 170 | °C | ASTM D1525 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (3.00 mm) | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 2.0 | hr | |
| Processing (Melt) Temp | 182 to 215 | °C | |
| Mold Temperature | 78.0 to 106 | °C | |
| Injection Pressure | 69.0 to 102 | MPa |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 2.0 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 1200.5-90A | RTP Company | TPU-Polyester | RTP |
| Tarnoform® 400 LS | Grupa Azoty S.A. | Acetal (POM) Copolymer | Tarnoform® |
| Carbotex K-40UVR | Kotec Corporation | PC | Carbotex |
| GUR® 4150 | Celanese Corporation | UHMWPE | GUR® |
| OnForce™ LFT LF6600-5013 Grey | PolyOne Corporation | Nylon 66 | OnForce™ LFT |