RTP 227H UV
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | RTP Company |
| Trademark: | RTP |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | CNTlQa_RTP-227H-UV.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Warning: The status of this material is 'Commercial: Limited Issue' The data for this material has not been recently verified. Please contact RTP Company for current information prior to specifying this grade. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| RoHS Compliance |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.47 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow | ASTM D955 | ||
| 3.18mm, injection molding | 0.70 | % | ASTM D955 |
| 6.35mm, injection molding | 0.90 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (Injection Molded) | 6200 | MPa | ASTM D638 |
| Tensile Strength | 59.0 | MPa | ASTM D638 |
| Tensile Elongation (Yield, Injection Molded) | 4.0 | % | ASTM D638 |
| Flexural Modulus (Injection Molded) | 6200 | MPa | ASTM D790 |
| Flexural Strength (Injection Molded) | 100 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (3.18 mm, Injection Molded) | 110 | J/m | ASTM D256 |
| Unnotched Izod Impact (3.18 mm) | 530 | J/m | ASTM D4812 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, unannealed, injection molded | 227 | °C | ASTM D648 |
| 1.8 MPa, unannealed, injection molded | 193 | °C | ASTM D648 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (1.50 mm) | HB | UL 94 |
| Additional Information |
|---|
| The value listed as Flammibility, UL 94, was tested in accordance with RTP Company methods. |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Rear Temperature | 274 - 293 | °C | |
| Middle Temperature | 274 - 293 | °C | |
| Front Temperature | 274 - 293 | °C | |
| Mold Temperature | 66.0 - 107 | °C | |
| Injection Pressure | 103 - 124 | MPa |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sanren F850EBA (On-spec.) | SINOPEC Shanghai Petrochemical Co. Ltd. | PP Homopolymer | Sanren |
| ResMart Repro HIPS Black | ResMart | PS (HIPS) | ResMart Repro |
| Zytel® FG77G33L NC010 | DuPont Performance Polymers | Nylon 612 | Zytel® |
| AIE PC 1010F-T6 | Asia International Enterprise (Hong Kong) Limited | PC | AIE PC |
| OTECH PVC OM7544-Molding | OTECH Corporation | PVC, Unspecified | OTECH PVC |