Telcar TELC 1000-92 is a high hardness, low density general purpose thermoplastic elastomer designed for interior injection molding applications in the automotive industry.

General Information
Features	Low Specific Gravity Low density Low liquidity Fill High hardness
Uses	Car interior parts
Appearance	Natural color
Forms	Particle
Processing Method	Injection molding

Physical	Nominal Value	Unit	Test Method
Specific Gravity	0.911	g/cm³	ASTM D792
Melt Mass-Flow Rate (MFR) (230°C/2.16 kg)	2.6	g/10 min	ASTM D1238
Molding Shrinkage - Flow			ASTM D955
180°C, 30 minutes	1.3	%	ASTM D955
24 hours	1.1	%	ASTM D955

Hardness	Nominal Value	Test Method
Durometer Hardness		ASTM D2240
Shaw D, 1 sec	49	ASTM D2240
Shaw D, 5 seconds	41	ASTM D2240

Mechanical	Nominal Value	Unit	Test Method
Flexural Modulus	290	MPa	ASTM D790

Elastomers	Nominal Value	Unit	Test Method
Tensile Stress			ASTM D412
Flow : 100% strain	9.60	MPa	ASTM D412
Transverse flow : 100% strain ¹	7.02	MPa	ASTM D412
Tensile Strength			ASTM D412
Flow : Yield	9.90	MPa	ASTM D412
Transverse flow : Yield ²	7.40	MPa	ASTM D412
Tensile Elongation			ASTM D412
Transverse flow : Fracture ³	370	%	ASTM D412
Flow : Fracture ⁴	270	%	ASTM D412
Tear Strength - Across Flow	87.0	kN/m	ASTM D624
Compression Set			ASTM D395
23°C, 22 hr	60	%	ASTM D395
70°C, 22 hr	74	%	ASTM D395
90°C, 70 hr	93	%	ASTM D395

Impact	Nominal Value	Unit	Test Method
Notched Izod Impact (-40°C)	No Break		ASTM D256
Dart Drop Impact (-30°C)	33.9	J	ASTM D3029
Tensile Impact Strength	471	kJ/m²	ASTM D1822

Aging	Nominal Value	Unit	Test Method
Change in Tensile Strength in Air			ASTM D573
110°C, 1008 hr	1.6	%	ASTM D573
125°C, 168 hr	4.3	%	ASTM D573
Change in Ultimate Elongation in Air			ASTM D573
110°C, 1008 hr	-43	%	ASTM D573
125°C, 168 hr	-40	%	ASTM D573
Change in Durometer Hardness in Air (support d, 110°C, 1008 hr)	1.7		ASTM D573

Thermal	Nominal Value	Unit	Test Method
Deflection Temperature Under Load			ASTM D648
0.45 MPa, not annealed	62.5	°C	ASTM D648
1.8 MPa, not annealed	40.7	°C	ASTM D648
Glass Transition Temperature	-55.9	°C	DSC
Linear thermal expansion coefficient			ASTM D696
Flow : -30 to 30°C	1.2E-4	cm/cm/°C	ASTM D696
Lateral : -30 to 30°C	1.2E-4	cm/cm/°C	ASTM D696

Flammability	Nominal Value	Unit	Test Method
Burning Rate	30	mm/min	ISO 3795

Fill Analysis	Nominal Value	Unit	Test Method
Apparent Viscosity (200°C, 206 sec^-1)	516	Pa·s	ASTM D3835

Additional Information
Instrumented Dart Impact Energy @ Yield, -40°C, 9000 in/min, Ductile Failure: 200 in-lbsInstrumented Dart Impact Deflection @ Break, -40°C, 9000 in/min, Ductile Failure: 1359 milsInstrumented Dart Impact Energy @ Break, -40°C, 9000 in/min, Ductile Failure: 350 in-lbsFogging, Kaake Buchler, 3 hrs, 100°C: 92Tear Strength, ASTM D1004, Die C: 364 lb/inHeat Aging Performance Izod Impact, 1000 hrs, 120°C: No BreakFlammability Burn Rate, FMVSS 302, Max 100, 30.2 mm/min: PassFlammability Burn Rate, FMVSS 302, Max 100, 1.2 in/min: PassPoisson's Ratio, ASTM D 638, @-35°C = 0.337, @+23°C = 0.419, @+85°C = 0.363

Additional Information

Instrumented Dart Impact Energy @ Yield, -40°C, 9000 in/min, Ductile Failure: 200 in-lbsInstrumented Dart Impact Deflection @ Break, -40°C, 9000 in/min, Ductile Failure: 1359 milsInstrumented Dart Impact Energy @ Break, -40°C, 9000 in/min, Ductile Failure: 350 in-lbsFogging, Kaake Buchler, 3 hrs, 100°C: 92Tear Strength, ASTM D1004, Die C: 364 lb/inHeat Aging Performance Izod Impact, 1000 hrs, 120°C: No BreakFlammability Burn Rate, FMVSS 302, Max 100, 30.2 mm/min: PassFlammability Burn Rate, FMVSS 302, Max 100, 1.2 in/min: PassPoisson's Ratio, ASTM D 638, @-35°C = 0.337, @+23°C = 0.419, @+85°C = 0.363

Legal statement
The information and recommendations contained in this bulletin are, to the best of our knowledge, accurate and reliable but no guarantee of their accuracy is made. All products are sold upon condition that purchasers shall make their own tests to determine the suitability of such products for their particular purposes and uses and purchaser assumes all risks and liability for the results of use of the products, including use in accordance with seller's recommendations. Nothing in this bulletin constitutes permission or a recommendation to practice or use any invention covered by any patent owned by this company or others. There is no warranty of merchantability and there are no other warranties for the products described. For detailed Product Stewardship information, please contact us. Any product of Teknor Apex, including product names, shall not be used or tested in medical or food contact applications without the prior written acknowledgement of Teknor Apex as to the intended use. Please note that some products may not be available in one or more countries.

Legal statement

The information and recommendations contained in this bulletin are, to the best of our knowledge, accurate and reliable but no guarantee of their accuracy is made. All products are sold upon condition that purchasers shall make their own tests to determine the suitability of such products for their particular purposes and uses and purchaser assumes all risks and liability for the results of use of the products, including use in accordance with seller's recommendations. Nothing in this bulletin constitutes permission or a recommendation to practice or use any invention covered by any patent owned by this company or others. There is no warranty of merchantability and there are no other warranties for the products described. For detailed Product Stewardship information, please contact us. Any product of Teknor Apex, including product names, shall not be used or tested in medical or food contact applications without the prior written acknowledgement of Teknor Apex as to the intended use. Please note that some products may not be available in one or more countries.

Injection	Nominal Value	Unit
Rear Temperature	171 - 193	°C
Middle Temperature	177 - 199	°C
Front Temperature	182 - 204	°C
Nozzle Temperature	188 - 210	°C
Processing (Melt) Temp	188 - 210	°C
Mold Temperature	25.0 - 65.6	°C
Injection Pressure	1.38 - 6.89	MPa
Injection Rate	Moderate-Fast
Back Pressure	0.172 - 0.345	MPa
Screw Speed	50 - 100	rpm
Cushion	3.81 - 25.4	mm

Extrusion	Nominal Value	Unit
Drying Temperature	80.0	°C
Drying Time	2.0	hr
Cylinder Zone 1 Temp.	166 - 188	°C
Cylinder Zone 2 Temp.	171 - 193	°C
Cylinder Zone 3 Temp.	177 - 199	°C
Cylinder Zone 5 Temp.	182 - 204	°C
Die Temperature	190 - 210	°C

Extrusion instructions
螺杆转速30 - 100 rpm

Note Message
1 .	51 mm/min
2 .	51 mm/min
3 .	51 mm/min
4 .	Type 1, 510mm/min

Category:	TPE , Thermoplastic Elastomer
Manufacturer:	Teknor Apex Company
Trademark:	Telcar®
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	CN4RCs_Telcar-TELC-1000-92.pdf
PRICE:	Order Products email sales@su-jiao.com

Resin Grade	Manufacturer	Category	Trademark
Sanren TB500T	SINOPEC Shanghai Petrochemical Co. Ltd.	PP, Unspecified	Sanren
Moharamplast MDPE MP3840U	Moharamplast S.A.E	MDPE	Moharamplast MDPE
AKROMID® B3 GF 15 S1 natural (3693)	AKRO-PLASTIC GmbH	Nylon 6	AKROMID®
INSPIRE™ 6025	Braskem America Inc.	PP Homopolymer	INSPIRE™
EPIMAX® ABS-808HG	Osterman & Company	ABS	EPIMAX®