ENGAGE™ 8452 EL
| Category: | TPO (POE) , Polyolefin Elastomer |
| Manufacturer: | The Dow Chemical Company |
| Trademark: | ENGAGE™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | CMqRbF_ENGAGE-8452-EL.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
ENGAGE™ 8452 EL Polyolefin Elastomer is an ethylene-octene copolymer that offers excellent toughness and softness. It has excellent compatibility with other polyolefins, allowing for efficient blending and coextrusion. It provides excellent flow properties and is efficiently cross-linked by peroxide, silane, or irradiation. When cross-linked, it gives exceptional heat aging, compression set, and weather resistance properties. Main Characteristics:
Applications:
Complies with:
|
| General Information | |
|---|---|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.875 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 3.0 | g/10 min | ASTM D1238 |
| Mooney Viscosity (ML 1+4, 121°C) | 11 | MU | ASTM D1646 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness | ASTM D2240 | ||
| Shore A, Compression Molded | 74 | ||
| Shore D, Compression Molded | 24 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus - 100% Secant 1(Compression Molded) | 3.00 | MPa | ASTM D638 |
| Tensile Strength 2(Break, Compression Molded) | 11.2 | MPa | ASTM D638 |
| Tensile Elongation 3(Break, Compression Molded) | 950 | % | ASTM D638 |
| Flexural Modulus | ASTM D790 | ||
| 1% Secant : Compression Molded | 16.5 | MPa | |
| 2% Secant : Compression Molded | 16.8 | MPa |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tear Strength 4 | 45.1 | kN/m | ASTM D624 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Glass Transition Temperature | -51.0 | °C | Internal Method |
| Vicat Softening Temperature | 48.0 | °C | ASTM D1525 |
| Melting Temperature (DSC) 5 | 66.0 | °C | Internal Method |
| Peak Crystallization Temperature (DSC) | 48.0 | °C | Internal Method |
| Note Message | |
|---|---|
| 1 . | 510 mm/min |
| 2 . | 510 mm/min |
| 3 . | 510 mm/min |
| 4 . | Die C |
| 5 . | 10°C/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Rilsan® Fine Powders ESY BLACK 7260 | Arkema | Nylon 11 | Rilsan® Fine Powders |
| PRE-ELEC® PE 1296 | Premix Oy | HDPE | PRE-ELEC® |
| RTP 800.5 TFE 10 | RTP Company | Acetal (POM) Copolymer | RTP |
| NEXT SIGNATURE PA6 GM40-300 | NEXT Specialty Resins, Inc. | Nylon 6 | NEXT SIGNATURE |
| TOTAL Polyethylene Lumicene® M 5220 (Blow Molding) | TOTAL Refining & Chemicals | mHDPE | TOTAL Polyethylene |