Qenos PE HDF895
| Category: | HDPE, MMW , High Density (MMW) Polyethylene |
| Manufacturer: | Qenos Pty Ltd |
| Trademark: | Qenos PE |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | CMR4up_Qenos-PE-HDF895.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
HDF895 is a medium molecular weight High Density Polyethylene grade. HDF895 is particularly suitable as a blend component in LDPE / LLDPE films to enhance stiffness. Suitability for use in any application should be determined by appropriate performance testing. |
| General Information | |
|---|---|
| Features |
|
| Agency Ratings |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.960 | g/cm³ | ASTM D1505 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 0.80 | g/10 min | ASTM D1238 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 18 | µm | |
| Secant Modulus | ASTM D882 | ||
| 2% Secant, MD | 750 | MPa | |
| 2% Secant, TD | 780 | MPa | |
| Tensile Strength | ASTM D882 | ||
| MD : Yield | 24.0 | MPa | |
| TD : Yield | 25.0 | MPa | |
| MD : Break | 44.0 | MPa | |
| TD : Break | 29.0 | MPa | |
| Tensile Elongation | ASTM D882 | ||
| MD : Break | 680 | % | |
| TD : Break | 980 | % | |
| Dart Drop Impact | < 50 | g | ASTM D1709 |
| Elmendorf Tear Strength | ASTM D1922 | ||
| MD | 9.0 | cN | |
| TD | 498.0 | cN |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TOTAL Polypropylene Aceso® PPM H350 | TOTAL Refining & Chemicals | PP Homopolymer | TOTAL Polypropylene |
| WELLAMID Nylon 6600 GV 40 HWCP | CP-Polymer-Technik GmbH & Co. KG | Nylon 66 | WELLAMID Nylon |
| Trexprene® A88BU | Mitsubishi Chemical Performance Polymers, Inc. | TPV | Trexprene® |
| KumhoSunny PC/PBT HCB9230 | Shanghai KumhoSunny Plastics Co., Ltd. | PC+PBT | KumhoSunny PC/PBT |
| POLYfill PP CPQ10015 FF | Polykemi AB | PP, Unspecified | POLYfill |