LNP™ THERMOCOMP™ 9X07430 compound
| Category: | PC+PBT , Polycarbonate + PBT |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ THERMOCOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | CIkiAP_LNP-THERMOCOMP-9X07430-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP THERMOCOMP 9X07430 is a compoud based on a PBT+PC Blend containing Glass Fiber, Talc. Added features of this material include: Opaque, Weatherable. Also known as: LNP* THERMOCOMP* Compound 9X07430 Product reorder name: 9X07430 |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.31 | g/cm³ | ASTM D792, ISO 1183 |
| Molding Shrinkage | |||
| Flow | 0.51 | % | Internal Method |
| Flow : 24 hr | 0.50 to 0.51 | % | ASTM D955 |
| Across Flow | 0.59 | % | Internal Method |
| Across Flow : 24 hr | 0.58 to 0.59 | % | ASTM D955 |
| Water Absorption | |||
| 24 hr, 50% RH | 0.11 | % | ASTM D570 |
| Equilibrium, 23°C, 50% RH | 0.16 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 3300 | MPa | ASTM D638 |
| -- | 3160 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Yield 2 | 57.0 | MPa | ASTM D638 |
| Yield | 60.0 | MPa | ISO 527-2/5 |
| Break 3 | 51.0 | MPa | ASTM D638 |
| Break | 56.0 | MPa | ISO 527-2/5 |
| Tensile Elongation | |||
| Yield 4 | 2.9 | % | ASTM D638 |
| Yield | 3.1 | % | ISO 527-2/5 |
| Break 5 | 4.8 | % | ASTM D638 |
| Break | 4.9 | % | ISO 527-2/5 |
| Flexural Modulus | |||
| 50.0 mm Span 6 | 3140 | MPa | ASTM D790 |
| -- 7 | 3020 | MPa | ISO 178 |
| Flexural Stress | |||
| -- | 97.0 | MPa | ISO 178 |
| Yield, 50.0 mm Span 8 | 99.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 80 | J/m | ASTM D256 |
| 23°C 9 | 8.7 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | 720 | J/m | ASTM D4812 |
| 23°C 10 | 47 | kJ/m² | ISO 180/1U |
| Instrumented Dart Impact | |||
| -30°C, Energy at Peak Load | 3.00 | J | ASTM D3763 |
| -30°C, Total Energy | 7.00 | J | ASTM D3763 |
| 23°C, Energy at Peak Load | 9.00 | J | ASTM D3763 |
| 23°C, Total Energy | 14.0 | J | ASTM D3763 |
| -- | 7.00 | J | ISO 6603-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 1.8 MPa, Unannealed, 3.20 mm | 102 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 64.0 mm Span 11 | 105 | °C | ISO 75-2/Af |
| CLTE | ASTM E831 | ||
| Flow : -40 to 40°C | 5.7E-5 | cm/cm/°C | |
| Transverse : -40 to 40°C | 8.3E-5 | cm/cm/°C |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 to 110 | °C | |
| Drying Time | 4.0 to 6.0 | hr | |
| Drying Time, Maximum | 24 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Rear Temperature | 245 to 270 | °C | |
| Middle Temperature | 255 to 275 | °C | |
| Front Temperature | 260 to 280 | °C | |
| Nozzle Temperature | 260 to 280 | °C | |
| Processing (Melt) Temp | 260 to 280 | °C | |
| Mold Temperature | 80.0 to 110 | °C | |
| Back Pressure | 0.300 to 0.700 | MPa |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | Type I, 5.0 mm/min |
| 3 . | Type I, 5.0 mm/min |
| 4 . | Type I, 5.0 mm/min |
| 5 . | Type I, 5.0 mm/min |
| 6 . | 1.3 mm/min |
| 7 . | 2.0 mm/min |
| 8 . | 1.3 mm/min |
| 9 . | 80*10*4 |
| 10 . | 80*10*4 |
| 11 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Quantum Composites QC-3100 | Quantum Composites Inc. | Vinyl Ester | Quantum Composites |
| Sindustris PC SG5010FA | Sincerity Australia Pty Ltd. | PC+ABS+Acrylic | Sindustris PC |
| Moplen HP500M | Shazand (Arak) Petrochemical Corporation | PP Homopolymer | Moplen |
| Karina BEIGE PVC COMPOUND -E 650-22/ 31 | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| POCAN® KU 1-7635 POS 151 000000 | LANXESS GmbH | PC+PBT | POCAN® |