| Category: | ABS , Acrylonitrile Butadiene Styrene |
| Manufacturer: | Chase Plastics Services Inc. |
| Trademark: | CP PRYME® ABS |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | CIZUBy_CPPRYMEABSA10089.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Prime ABS, General Purpose |
| General Information | |
|---|---|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.04 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (230°C/3.8 kg) | 5.6 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow (3.20 mm) | 0.50 - 0.80 | % | ASTM D955 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 112 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2270 | MPa | ASTM D638 |
| Tensile Strength | ASTM D638 | ||
| Yield | 44.0 | MPa | ASTM D638 |
| Fracture | 33.0 | MPa | ASTM D638 |
| Tensile Elongation | ASTM D638 | ||
| Yield | 2.0 | % | ASTM D638 |
| Fracture, 23°C | 25 | % | ASTM D638 |
| Flexural Modulus (50.0 mm Span) | 2300 | MPa | ASTM D790 |
| Flexural Strength (Yield, 50.0 mm Span) | 70.3 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 320 | J/m | ASTM D256 |
| Instrumented Dart Impact | 30.1 | J | ASTM D3763 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, unannealed, 3.20mm | 93.9 | °C | ASTM D648 |
| 1.8 MPa, unannealed, 3.20mm | 80.0 | °C | ASTM D648 |
| Vicat Softening Temperature | 81.1 | °C | ASTM D1525 |
| Linear thermal expansion coefficient | ASTM E831 | ||
| Flow : -40 to 40°C | 8.8E-5 | cm/cm/°C | ASTM E831 |
| Lateral : -40 to 40°C | 8.8E-5 | cm/cm/°C | ASTM E831 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82 - 93 | °C | |
| Drying Time | 2.0 - 4.0 | hr | |
| Suggested Max Moisture | 0.10 | % | |
| Rear Temperature | 188 - 210 | °C | |
| Middle Temperature | 204 - 227 | °C | |
| Front Temperature | 216 - 238 | °C | |
| Nozzle Temperature | 218 - 260 | °C | |
| Mold Temperature | 49 - 71 | °C | |
| Back Pressure | 0.345 - 0.689 | MPa |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Resirene 2220 | Resirene, S.A. de C.V. | PS (MIPS) | Resirene |
| Detectaseal® XS7H | Precision Polymer Engineering Ltd. | Silicone | Detectaseal® |
| Edgetek™ AS-000/000 AS BLACK | PolyOne Corporation | ABS | Edgetek™ |
| ELASTOSIL® R plus 4000/60 | Wacker Chemie AG | Silicone | ELASTOSIL® R plus |
| Hanwha Total PE P200CB | HANWHA TOTAL PETROCHEMICALS Co., Ltd. | HDPE | Hanwha Total PE |