Polifil® Nylon 628-33GF
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | The Plastics Group |
| Trademark: | Polifil® Nylon |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | CI4OGe_Polifil-Nylon-628-33GF.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Polifil® GFN/MRN 6/6 reinforced series of compounds offer superior strength, rigidity, and creep resistance. Glass fibers provide excellent thermal and dimensional stability while maintaining good heat and chemical resistance. Polifil® GFN/MRN are excellent candidates for bike components and fuel caps, as well as other automotive components. Standard processing techniques are applicable. Use this information as a guide to aid you in selecting the proper resin for your application. TPG will custom compound and fine-tune our formulations for your application. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.38 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow (3.18 mm) | 0.30 | % | ASTM D955 |
| Water Absorption (24 hr) | 0.75 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 120 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C) | 9650 | MPa | ASTM D638 |
| Tensile Strength (23°C) | 165 | MPa | ASTM D638 |
| Tensile Elongation | ASTM D638 | ||
| Yield, 23°C | 3.0 | % | |
| Break, 23°C | 3.0 | % | |
| Flexural Modulus - Tangent (23°C) | 8270 | MPa | ASTM D790 |
| Flexural Strength (23°C) | 228 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 110 | J/m | ASTM D256 |
| Gardner Impact (23°C, 12.7 mm) | 0.452 | J | ASTM D3029 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed | 254 | °C | |
| 1.8 MPa, Unannealed | 249 | °C |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 104 | °C | |
| Drying Time | 2.0 | hr | |
| Rear Temperature | 288 | °C | |
| Middle Temperature | 274 | °C | |
| Front Temperature | 282 | °C | |
| Nozzle Temperature | 288 | °C | |
| Processing (Melt) Temp | 282 to 304 | °C | |
| Mold Temperature | 37.8 to 93.3 | °C | |
| Injection Rate | Fast | ||
| Back Pressure | 0.172 to 0.517 | MPa | |
| Screw Speed | 30 to 60 | rpm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TPUCO® TPUE-UEH90 | Taiwan PU Corporation | TPU-Polyether | TPUCO® |
| Badadur® PBT8 FR HF | Bada AG | PBT | Badadur® |
| Gallonprene® GP420-5003 | Shenzhen Sungallon Rubber & Plastic Corporation Limited | TPE | Gallonprene® |
| Geon™ Vinyl Fittings M1018 | PolyOne Corporation | PVC, Rigid | Geon™ Vinyl Fittings |
| Moplen RP225N | LyondellBasell Industries | PP Random Copolymer | Moplen |