Compound based on Polyamide 66 (PA 66). Toughened. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.07 | g/cm³ | ISO 1183 |
| Molding Shrinkage 1 | ISO 294-4 | ||
| Across Flow : 2.00 mm | 1.3 to 1.6 | % | |
| Flow : 2.00 mm | 1.3 to 1.7 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | ISO 527-2/1 | ||
| 23°C | 1500 | MPa | |
| 60°C | 500 | MPa | |
| 90°C | 350 | MPa | |
| 120°C | 200 | MPa | |
| 150°C | 200 | MPa |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -20°C | 20 | kJ/m² | |
| 23°C | 100 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179/1eU | ||
| -20°C | No Break | ||
| 23°C | No Break | ||
| Notched Izod Impact | ASTM D256A | ||
| -20°C, 3.20 mm | 210 | J/m | |
| 23°C, 3.20 mm | No Break |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 155 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 45.0 | °C | ISO 75-2/A |
| Continuous Use Temperature 2 | 90.0 | °C | |
| Vicat Softening Temperature | 195 | °C | ISO 306/B50 |
| CLTE - Flow (30 to 100°C) | 7.0E-5 | cm/cm/°C | ASTM D696 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 90.0 to 100 | °C | |
| Drying Time | 3.0 | hr | |
| Processing (Melt) Temp | 260 to 290 | °C | |
| Mold Temperature | 60.0 to 80.0 | °C | |
| Injection Rate | Moderate |
| Note Message | |
|---|---|
| 1 . | at 60 MPa of cavity pressure |
| 2 . | 20,000 hr |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 2800 B-55A Z | RTP Company | TPV | RTP |
| REXtac® APAO RT 1215 | Huntsman Corporation | PAO | REXtac® APAO |
| Shandong PA612 A5RG7301 | Shandong Dongchen Engineering Plastics Co., Ltd. | Nylon 612 | Shandong PA612 |
| UBESTA 3012 U | UBE Engineering Plastics, S.A. | Nylon 12 | UBESTA |
| ACCUTECH™ HP0339G20M10CL | ACLO Compounders Inc. | PP Homopolymer | ACCUTECH™ |