Anjacom® 100X-UV
| Category: | PC , Polycarbonate |
| Manufacturer: | Almaak International GmbH |
| Trademark: | Anjacom® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | CGqSMU_Anjacom-100X-UV.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Anjacom® 100X-UV is a Polycarbonate (PC) material. It is available in Europe. Important attributes of Anjacom® 100X-UV are:
|
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density (23°C) | 1.20 | g/cm³ | ISO 1183 |
| Melt Volume-Flow Rate (MVR) (300°C/1.2 kg) | 10.0 | cm³/10min | ISO 1133 |
| Molding Shrinkage | ISO 294-4 | ||
| Across Flow | 0.60 | % | |
| Flow | 0.60 | % | |
| Water Absorption | ISO 62 | ||
| 23°C, 24 hr | 0.35 | % | |
| Equilibrium, 23°C, 50% RH | 0.15 | % | |
| Relative Viscosity | 1.30 | ISO 1628 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2400 | MPa | ISO 527-2/1 |
| Tensile Stress (Yield) | 63.0 | MPa | ISO 527-2/50 |
| Tensile Strain (Break) | 6.0 | % | ISO 527-2/50 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 15 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength (23°C) | No Break | ISO 179/1eU |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 139 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 130 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 147 | °C | ISO 306/B50 |
| Melting Temperature | 148 | °C | DSC |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Electric Strength | 30 | kV/mm | IEC 60243-1 |
| Comparative Tracking Index | 250 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.60 mm) | V-2 | UL 94 | |
| Glow Wire Flammability Index (4.00 mm) | 850 | °C | IEC 60695-2-12 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 120 | °C | |
| Drying Time | 2.0 to 5.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Processing (Melt) Temp | 280 to 300 | °C | |
| Mold Temperature | 85.0 to 120 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Maxelast® P1957TA | Nantong Polymax Elastomer Technology, Co., Ltd | TPE | Maxelast® |
| SAMAT EP5001A(f1) | POLYROCKS CHEMICAL CO., LTD | PP, Unspecified | SAMAT |
| Braskem PE LL6800N | Braskem | LLDPE | Braskem PE |
| KOPLA PA6 KNG1030 | KOPLA Co., Ltd. | Nylon 6 | KOPLA PA6 |
| Huaxia Shenzhou FKM DS2603-1 | Shandong Huaxia Shenzhou New Material Co., Ltd. | Fluorelastomer | Huaxia Shenzhou |