Generic PET - Glass Fiber
| Category: | PET , Polyethylene Terephthalate |
| Manufacturer: | Generic |
| Trademark: | Generic |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | CGUf67_Generic-PET---Glass-Fiber.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
This data represents typical values that have been calculated from all products classified as: Generic PET - Glass Fiber This information is provided for comparative purposes only. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 1.44 - 1.71 | g/cm³ | ASTM D792 |
| 23°C | 1.38 - 1.78 | g/cm³ | ISO 1183 |
| Molding Shrinkage | |||
| Flow : 23°C | 0.17 - 0.53 | % | ASTM D955 |
| Transverse flow : 23°C | 0.54 - 1.1 | % | ASTM D955 |
| 23°C | 0.20 - 1.0 | % | ISO 294-4 |
| Water Absorption | |||
| 23°C, 24 hr | 0.044 - 0.061 | % | ASTM D570 |
| 23°C, 24 hr | 0.040 - 0.60 | % | ISO 62 |
| Saturated, 23°C | 0.23 - 0.91 | % | ISO 62 |
| Equilibrium, 23°C | 0.045 - 0.20 | % | ASTM D570 |
| Equilibrium, 23°C, 50% RH | 0.18 - 0.21 | % | ISO 62 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness | |||
| 23°C | 116 - 122 | ASTM D785 | |
| 23°C | 99 - 123 | ISO 2039-2 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| 23°C | 4200 - 16700 | MPa | ASTM D638 |
| 23°C | 4500 - 19200 | MPa | ISO 527-2 |
| Tensile Strength | |||
| Yield, 23°C | 80.0 - 176 | MPa | ASTM D638 |
| Yield, 23°C | 125 - 161 | MPa | ISO 527-2 |
| Fracture, 23°C | 96.3 - 197 | MPa | ASTM D638 |
| Fracture, 23°C | 78.4 - 210 | MPa | ISO 527-2 |
| 23°C | 0.866 - 195 | MPa | ASTM D638 |
| Tensile Elongation | |||
| Yield, 23°C | 2.0 - 4.0 | % | ASTM D638 |
| Yield, 23°C | 2.0 | % | ISO 527-2 |
| Fracture, 23°C | 2.0 - 3.4 | % | ASTM D638 |
| Fracture, 23°C | 1.4 - 3.2 | % | ISO 527-2 |
| Flexural Modulus | |||
| 23°C | 5790 - 13800 | MPa | ASTM D790 |
| 23°C | 3900 - 12300 | MPa | ISO 178 |
| Flexural Strength | |||
| 23°C | 1.64 - 290 | MPa | ASTM D790 |
| 23°C | 129 - 271 | MPa | ISO 178 |
| Yield, 23°C | 148 - 223 | MPa | ASTM D790 |
| Fracture, 23°C | 170 - 222 | MPa | ASTM D790 |
| Compressive Strength (23°C) | 136 - 235 | MPa | ASTM D695 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 5.9 - 11 | kJ/m² | ISO 179 |
| Charpy Unnotched Impact Strength (23°C) | 29 - 65 | kJ/m² | ISO 179 |
| Notched Izod Impact | |||
| 23°C | 59 - 120 | J/m | ASTM D256 |
| 23°C | 5.9 - 10 | kJ/m² | ISO 180 |
| Notched Izod Impact (23°C) | 5.00 - 6.05 | kJ/m² | ASTM D256 |
| Unnotched Izod Impact | |||
| 23°C | 260 - 970 | J/m | ASTM D256 |
| 23°C | 29 - 46 | kJ/m² | ISO 180 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, not annealed | 229 - 251 | °C | ASTM D648 |
| 0.45 MPa, not annealed | 219 - 252 | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 209 - 233 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 199 - 241 | °C | ISO 75-2/A |
| Continuous Use Temperature | 110 - 150 | °C | ASTM D794 |
| Vicat Softening Temperature | |||
| -- | 234 - 241 | °C | ASTM D1525 |
| -- | 215 - 241 | °C | ISO 306 |
| Melting Temperature | |||
| -- | 245 - 256 | °C | ISO 3146 |
| -- | 250 - 256 | °C | ISO 11357-3 |
| -- | 245 - 255 | °C | ASTM D3418 |
| Linear thermal expansion coefficient | |||
| Flow | 1.9E-5 - 4.5E-5 | cm/cm/°C | ASTM D696 |
| Flow | 4.0E-6 - 5.8E-5 | cm/cm/°C | ASTM E831 |
| Flow | 4.0E-6 - 3.4E-5 | cm/cm/°C | ISO 11359-2 |
| Lateral | 3.1E-5 - 1.1E-4 | cm/cm/°C | ASTM E831 |
| Lateral | 3.5E-5 - 1.2E-4 | cm/cm/°C | ISO 11359-2 |
| Thermal Conductivity (23°C) | 0.27 - 1.7 | W/m/K | ASTM C177 |
| RTI Elec | 139 - 155 | °C | UL 746 |
| RTI Imp | 75.0 - 155 | °C | UL 746 |
| RTI | 75.0 - 155 | °C | UL 746 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | |||
| -- | 1.0E+13 - 1.0E+14 | ohms | ASTM D257 |
| -- | 7.6E+13 - 1.1E+15 | ohms | IEC 60093 |
| Volume Resistivity (23°C) | 1.0E+13 - 2.5E+16 | ohms·cm | ASTM D257, IEC 60093 |
| Dielectric Strength | |||
| 23°C | 19 - 34 | kV/mm | ASTM D149 |
| 23°C | 21 - 34 | kV/mm | IEC 60243-1 |
| Dielectric Constant | |||
| 23°C | 3.00 - 4.02 | ASTM D150 | |
| 23°C | 3.66 | IEC 60250 | |
| Dissipation Factor | |||
| 23°C | 4.9E-3 - 0.022 | ASTM D150 | |
| 23°C | 1.0E-3 - 0.020 | IEC 60250 | |
| Arc Resistance | 96.0 - 128 | sec | ASTM D495 |
| Comparative Tracking Index | 195 - 251 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Glow Wire Flammability Index | 743 - 960 | °C | IEC 60695-2-12 |
| Glow Wire Ignition Temperature | 650 - 968 | °C | IEC 60695-2-13 |
| Oxygen Index | |||
| -- | 24 - 32 | % | ASTM D2863 |
| -- | 19 - 36 | % | ISO 4589-2 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 119 - 131 | °C | |
| Drying Time | 3.0 - 7.0 | hr | |
| Dew Point | -40.0 - -39.4 | °C | |
| Suggested Max Moisture | 0.020 - 0.021 | % | |
| Suggested Max Regrind | 22 | % | |
| Hopper Temperature | 35.0 - 60.0 | °C | |
| Rear Temperature | 245 - 284 | °C | |
| Middle Temperature | 255 - 283 | °C | |
| Front Temperature | 265 - 283 | °C | |
| Nozzle Temperature | 254 - 325 | °C | |
| Processing (Melt) Temp | 274 - 290 | °C | |
| Mold Temperature | 60.0 - 136 | °C | |
| Injection Pressure | 8.00 - 86.7 | MPa | |
| Holding Pressure | 78.9 - 80.0 | MPa | |
| Back Pressure | 0.0862 - 7.50 | MPa | |
| Screw Speed | 43 - 94 | rpm |
| Injection instructions |
|---|
| This data represents typical values that have been calculated from all products classified as: Generic PET - Glass FiberThis information is provided for comparative purposes only. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Gallonprene® GP100-6501 | Shenzhen Sungallon Rubber & Plastic Corporation Limited | TPE | Gallonprene® |
| Huafon JF-S-8050A | Huafon Group Co., Ltd. | PUR, Unspecified | Huafon |
| Sylvin 86007-70 Clear 876 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| Sylvin 6426-70UV Natural | Sylvin Technologies Incorporated | PVC+NBR | Sylvin |
| CP PRYME® ABS A100-2 | Chase Plastics Services Inc. | ABS | CP PRYME® ABS |