SCHULAMID® 612 HV H 5003
| Category: | Nylon 612 , Polyamide 612 |
| Manufacturer: | A. Schulman Europe |
| Trademark: | SCHULAMID® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | CDgo8I_SCHULAMID-612-HV-H-5003.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Impact modified Polyamide 612, heatstabilized for injection molding |
| General Information | |
|---|---|
| Processing Method |
|
| Resin ID (ISO 1043) |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.05 | -- | g/cm³ | ISO 1183/A |
| Melt Volume-Flow Rate (MVR) (245°C/5.0 kg) | 8.50 | -- | cm³/10min | ISO 1133 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | 2000 | 920 | MPa | ISO 527-2/1A/1 |
| Tensile Stress (Yield) | 50.0 | 37.0 | MPa | ISO 527-2/1A/50 |
| Tensile Strain (Yield) | 4.8 | 18 | % | ISO 527-2/1A/50 |
| Nominal Tensile Strain at Break | 50 | 220 | % | ISO 527-2/1A/50 |
| Flexural Modulus 1 | 1500 | -- | MPa | ISO 178 |
| Flexural Stress 2 | ISO 178 | |||
| 3.5% strain | 47.0 | -- | MPa | ISO 178 |
| 6.7% strain | 60.0 | -- | MPa | ISO 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | |||
| -40°C | 15 | -- | kJ/m² | ISO 179/1eA |
| -30°C | 17 | -- | kJ/m² | ISO 179/1eA |
| 23°C | 75 | 110 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength | ISO 179/1eU | |||
| -40°C | No Break | -- | ISO 179/1eU | |
| -30°C | No Break | -- | ISO 179/1eU | |
| 23°C | No Break | No Break | ISO 179/1eU |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature | ||||
| 0.45 MPa, not annealed | 119 | -- | °C | ISO 75-2/Bf |
| 1.8 MPa, not annealed | 53.0 | -- | °C | ISO 75-2/Af |
| Vicat Softening Temperature | ||||
| -- | 205 | -- | °C | ISO 306/A50 |
| -- | 155 | -- | °C | ISO 306/B50 |
| Additional Information |
|---|
| 干燥 1.) Not for use in food contact applications2.) Not for use in medical or pharmaceutical applications |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | 2.0 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| XANTAR® LDS 3730 | Mitsubishi Engineering-Plastics Corp | PC | XANTAR® LDS |
| ICORENE® 1613 | ICO Polymers EMEA, A Division of A. Schulman | LMDPE | ICORENE® |
| Karina CLEAR PVC COMPOUND 80/229-IS-RG | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| Plexiglas® Satinice df22 7H | Evonik Industries AG | Acrylic (PMMA) | Plexiglas® |
| Trilliant™ HC HC3610-0001 HI Natural | PolyOne Corporation | PC+PBT | Trilliant™ HC |