AFFINITY™ PT 1450G1
| Category: | POP , Polyolefin Plastomer |
| Manufacturer: | The Dow Chemical Company |
| Trademark: | AFFINITY™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | CDXZz5_AFFINITY-PT-1450G1.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
AFFINITY™ PT 1450G1 Polyolefin Plastomer is produced via INSITE™ Technology. It is an ethylene alpha-olefin resin for monolayer and coextrusion coating that offers excellent low temperature seal initiation, ultimate seal strength, adhesion to (OPP) and good taste and odor performance. Note: It is the responsibility of the manufacturer of the food contact article to ensure the article is suitable for its intended use. Manufacturers should be aware that foods with a high oil content may compromise the integrity of the packaging. |
| General Information | |
|---|---|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.902 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 7.5 | g/10 min | ASTM D1238 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Seal Initiation Temperature 1(25 µm) | 82.8 | °C | Internal method |
| Can be bonded to OPP 2 | Internal method | ||
| 316°C | 0.13 | kN/m | Internal method |
| 288°C | 0.18 | kN/m | Internal method |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 77.2 | °C | ASTM D1525 |
| Melting Temperature (DSC) | 97.8 | °C | Internal method |
| Extrusion | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Melt Temperature | 288 - 316 | °C | |
| Neck-in (316°C, 25.4 µm) | 134.6 | mm | Internal method |
| Minimum coating thickness | µm | Internal method | |
| Minimum coating weight | g/m² | Internal method |
| Extrusion instructions |
|---|
| 挤出涂层薄膜的制造条件： 挤塑机：Black Clawson 螺杆尺寸：3.5 英寸 (90 mm)；30:1 L/D 模具间隙：20 密尔 (0.508 mm) 冷却辊温度：57°F (14°C) 熔体温度：600°F (315°C) 输出：250 磅/小时 气隙：6 英寸 (150 mm) |
| Note Message | |
|---|---|
| 1 . | 1.0 Mill (25 µm) coating applied to 50 pounds of kraft paper. Achieve a temperature of 1 psig (4.4 N/25.4mm) heat seal strength. Heat seal strength, Topwave HT tester, 0.5 S holding pressure, 40 psi pressure, pulling speed 150 mm/s. |
| 2 . | 1.0 Mill (25 µm) coating applied to 50 pounds of kraft paper. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Shanghai Ofluorine PVDF 9201F | Shanghai Ofluorine Chemical Technology Co., Ltd | PVDF | Shanghai Ofluorine PVDF |
| Styrolution PS 5600/5601 | INEOS Styrolution Group GmbH | PS (HIPS) | Styrolution PS |
| SURFACEMASTER® 905 | Cytec Industries Inc. | Epoxy | SURFACEMASTER® |
| Fainplast PVC CRK 84 | Fainplast Compounds S.r.l | PVC, Unspecified | Fainplast PVC |
| DIAMALOY ENGINEERED ALLOYS 808 C8 WW | Network Polymers, Inc. | PC Alloy | DIAMALOY ENGINEERED ALLOYS |