Ultraform® S 2320 003 UNC Q600
| Category: | Acetal (POM) Copolymer , Acetal (POM) Copolymer |
| Manufacturer: | BASF Corporation |
| Trademark: | Ultraform® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | CDMzuv_Ultraform-S-2320-003-UNC-Q600.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Ultraform S 2320 003 UNC Q600 is an easy flowing and rapidly freezing injection molding POM grade. Contains a mold release agent. Applications Typical applications include difficult, thin-walled parts. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Forms |
|
| Processing Method |
|
| Multi-Point Data |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.40 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Volume-Flow Rate (MVR) (190°C/2.16 kg) | 11.0 | cm³/10min | ISO 1133 |
| Molding Shrinkage | |||
| Flow : 3.18 mm | 2.0 | % | |
| Across Flow | 2.1 | % | ISO 294-4 |
| Flow | 2.1 | % | ISO 294-4 |
| Water Absorption | |||
| Saturation | 0.80 | % | ASTM D570 |
| Saturation, 23°C | 0.80 | % | ISO 62 |
| Equilibrium, 50% RH | 0.20 | % | ASTM D570 |
| Equilibrium, 23°C, 50% RH | 0.20 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C) | 2700 | MPa | ISO 527-2 |
| Tensile Strength | |||
| Yield, 23°C | 65.0 | MPa | ASTM D638, ISO 527-2 |
| Yield, -40°C | 93.0 | MPa | ISO 527-2 |
| Yield, 80°C | 33.0 | MPa | ISO 527-2 |
| Tensile Elongation (Yield, 23°C) | 9.0 | % | ASTM D638, ISO 527-2 |
| Nominal Tensile Strain at Break (23°C) | 28 | % | ISO 527-2 |
| Tensile Creep Modulus | ISO 899-1 | ||
| 1 hr | 1900 | MPa | |
| 1000 hr | 1300 | MPa | |
| Flexural Modulus (23°C) | 2620 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179 | ||
| -30°C | 5.0 | kJ/m² | |
| 23°C | 5.5 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179 | ||
| -30°C | 170 | kJ/m² | |
| 23°C | 180 | kJ/m² | |
| Notched Izod Impact | ASTM D256 | ||
| -40°C | 50 | J/m | |
| 23°C | 60 | J/m |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed | 160 | °C | ASTM D648 |
| 1.8 MPa, Unannealed | 110 | °C | ASTM D648 |
| 1.8 MPa, Unannealed | 100 | °C | ISO 75-2/A |
| Peak Melting Temperature | 167 | °C | ASTM D3418, ISO 3146 |
| CLTE - Flow | |||
| -- | 6.0E-5 | cm/cm/°C | ASTM E831 |
| -- | 1.1E-4 | cm/cm/°C |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity 1 | 1.0E+13 | ohms | ASTM D257, IEC 60093 |
| Volume Resistivity | |||
| 1.50 mm | 1.0E+13 | ohms·cm | ASTM D257 |
| -- | 1.0E+13 | ohms·cm | IEC 60093 |
| Electric Strength | 40 | kV/mm | IEC 60243-1 |
| Dielectric Constant | IEC 60250 | ||
| 100 Hz | 3.80 | ||
| 1 MHz | 3.80 | ||
| Dissipation Factor | IEC 60250 | ||
| 100 Hz | 1.0E-3 | ||
| 1 MHz | 5.0E-3 | ||
| Comparative Tracking Index | 600 | V | IEC 60112 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 to 110 | °C | |
| Drying Time | 2.0 to 4.0 | hr | |
| Suggested Max Moisture | 0.15 | % | |
| Processing (Melt) Temp | 190 to 230 | °C | |
| Mold Temperature | 60.0 to 120 | °C | |
| Injection Pressure | 3.50 to 7.00 | MPa |
| Note Message | |
|---|---|
| 1 . | 1.5 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Toyolac® TM335-GM1 | Toray Resin Company | ABS | Toyolac® |
| EMLON® 66 GFR 15 IM | EMAS Plastik San.Tic.AS. | Nylon 66 | EMLON® |
| ISOPAK® 547 | Great Eastern Resins Industrial Co Ltd (GRECO) | ABS | ISOPAK® |
| Optix® CA-927 | Plaskolite West, Inc. | Acrylic (PMMA) | Optix® |
| Starex VH-0800 E | LOTTE ADVANCED MATERIALS CO., LTD. | ABS | Starex |