LNP™ LUBRICOMP™ WFL369 compound
| Category: | PBT , Polybutylene Terephthalate |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ LUBRICOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | CCUZF8_LNPLUBRICOMPWFL369compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP LUBRICOMP WFL369 is a compound based on Polybutylene Terephalate resin containing Glass Fiber, PTFE. Added features include: Flame Retardant, Internally Lubricated. Also known as: LNP* LUBRICOMP* Compound WFL-4036 FR Product reorder name: WFL369 |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.79 | g/cm³ | ISO 1183 |
| Molding Shrinkage - Flow | 0.20 | % | Internal method |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 11000 | MPa | ISO 527-2/1 |
| Tensile Stress (Break) | 96.0 | MPa | ISO 527-2/5 |
| Tensile Strain (Break) | 1.4 | % | ISO 527-2/5 |
| Flexural Modulus 1 | 8500 | MPa | ISO 178 |
| Flexural Stress | 124 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact 2(23°C) | 7.0 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact Strength 3(23°C) | 20 | kJ/m² | ISO 180/1U |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature 4(1.8 MPa, Unannealed, 64.0 mm Span) | 202 | °C | ISO 75-2/Af |
| Linear thermal expansion coefficient | ISO 11359-2 | ||
| Flow : 23 to 60°C | 2.9E-5 | cm/cm/°C | ISO 11359-2 |
| Lateral : 23 to 60°C | 8.2E-5 | cm/cm/°C | ISO 11359-2 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (1.50 mm) | V-0 | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 121 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.050 | % | |
| Rear Temperature | 232 - 243 | °C | |
| Middle Temperature | 243 - 254 | °C | |
| Front Temperature | 249 - 260 | °C | |
| Processing (Melt) Temp | 243 - 260 | °C | |
| Mold Temperature | 82.2 - 98.9 | °C | |
| Back Pressure | 0.172 - 0.344 | MPa | |
| Screw Speed | 30 - 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | 80*10*4 |
| 3 . | 80*10*4 |
| 4 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Kumho ABS 740 | Korea Kumho Petrochemical Co., Ltd. | ABS | Kumho ABS |
| Karina CLEAR PVC COMPOUND 65/200 | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| K-Bin Rigid PVC KBD-3045 | K-Bin, Inc. | PVC, Unspecified | K-Bin Rigid PVC |
| OPTODYNE™ UV-3100 | DAIKIN AMERICA, INC. | Epoxy | OPTODYNE™ |
| VALOX™ V3900WX resin | SABIC Innovative Plastics Asia Pacific | PC+PBT | VALOX™ |