Propafilm™ RDU85
| Category: | PP Alloy , Polypropylene Alloy |
| Manufacturer: | Innovia Films Ltd. |
| Trademark: | Propafilm™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | CBUkGv_Propafilm-RDU85.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
High Barrier Differentially Coated Film Biaxially oriented polypropylene (BOPP) film coated on one side with a high barrier aqueous dispersion of polyvinylidene chloride (PVdC) copolymer, the other side coated with an aqueous acrylic dispersion. RDU85/100 are suitable for use as a single film or in laminations for overwrapping and form-fill-seal packaging especially in the bakery, cookie and confectionery industries. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Molding Shrinkage | Internal Method | ||
| Flow : 121°C, 1 min | 4.0 | % | |
| Flow : 129°C, 1 min | 7.0 | % | |
| Across Flow : 129°C, 1 min | 1.0 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Coefficient of Friction | ASTM D1894 | ||
| vs. Itself - Dynamic, Outside/Outside | 0.20 to 0.30 | ||
| vs. Itself - Static, Outside/Outside | 0.20 to 0.30 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 2200 | µm | |
| Seal Strength | Internal Method | ||
| -- 1 | 0.15 | N/mm | |
| -- 2 | 0.15 | N/mm | |
| Seal Initiation Temperature | Internal Method | ||
| -- 3 | 85.0 to 146 | °C | |
| -- 4 | 104 to 146 | °C | |
| Oxygen Permeability | ASTM F1927 | ||
| 23°C, 85% RH | 0.16 | cm³·mm/m²/atm/24 hr | |
| 25°C, 0% RH | 0.16 | cm³·mm/m²/atm/24 hr | |
| Water Vapor Transmission Rate (38°C, 90% RH) | 4.0 | g/m²/24 hr | ASTM F1770 |
| Yield | 51.0 | m²/kg | Internal Method |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (45°) | 100 | ASTM D2457 | |
| Haze 5 | 2.0 to 3.0 | % | ASTM D1003 |
| Note Message | |
|---|---|
| 1 . | PVdC/PVdC; 265°F; 2secs; 15psi |
| 2 . | Acrylic/Acrylic; 265°F; 2secs; 15psi |
| 3 . | Acrylic/Acrylic; 2secs; 15psi |
| 4 . | PVdC/PVdC; 2secs; 15psi |
| 5 . | Wide angle; 2.5° |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Starflex GM1810BE | LyondellBasell Industries | mLLDPE | Starflex |
| Macromeric® 0103-212a NT | Saco Polymers | Polyolefin, Unspecified | Macromeric® |
| Marlex® HMN TR-938G | Chevron Phillips Chemical Company LLC | MDPE | Marlex® |
| Sylvin 3280-55 Natural | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| Sylvin 8960-65FUV White 1465 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |