Maxxam™ NR-218.S001-8080
| Category: | PP, Unspecified , Polypropylene |
| Manufacturer: | PolyOne Corporation |
| Trademark: | Maxxam™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | CBSsSr_Maxxam-NR-218-S001-8080.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Mineral reinforced PP, good heat and UV stability |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.04 | g/cm³ | ASTM D792 |
| Molding Shrinkage | 0.90 - 1.1 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1 | 26.5 | MPa | ASTM D638 |
| Tensile Elongation 2(Break) | 40 | % | ASTM D638 |
| Flexural Modulus 3 | 2210 | MPa | ASTM D790 |
| Flexural Strength 4 | 39.5 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (Injection Molded) | 34 | J/m | ASTM D256A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (0.45 MPa, Unannealed) | 119 | °C | ASTM D648 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 - 85.0 | °C | |
| Drying Time | 4.0 - 6.0 | hr | |
| Processing (Melt) Temp | 200 - 240 | °C | |
| Mold Temperature | 30.0 - 60.0 | °C |
| Injection instructions |
|---|
| Injection Pressure: MED-HIGHHold Pressure: MED-HIGHScrew Speed: MODERATEBack Pressure: LOW |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 50 mm/min |
| 3 . | 1.3 mm/min |
| 4 . | 1.3 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SABIC® HDPE ICP5008 | Saudi Basic Industries Corporation (SABIC) | HDPE | SABIC® HDPE |
| SNOLEN® EB 1.4/46 | JSC Gazprom neftekhim Salavat | HDPE | SNOLEN® |
| Zhongfa PC G2810 | Yuyao Zhongfa Engineering Plastics Co. Ltd. | PC | Zhongfa |
| ASI POLYETHYLENE LP 477-01 | A. Schulman Inc. | HDPE | ASI POLYETHYLENE |
| Kepamid® 2330GFH | Korea Engineering Plastics Co., Ltd | Nylon 66 | Kepamid® |