LNP™ STAT-KON™ DX05305C compound
| Category: | PC , Polycarbonate |
| Manufacturer: | SABIC Innovative Plastics Asia Pacific |
| Trademark: | LNP™ STAT-KON™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | CB38K2_LNP-STAT-KON-DX05305C-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP STAT-KON DX05305C is a compound based on Polycarbonate resin containing Carbon Powder. Added features of this material include: Electrically Conductive, Clean Compounding System. Also known as: LNP* STAT-KON* Compound PDX-D-05305 CCS Product reorder name: DX05305C |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.22 | g/cm³ | ASTM D792, ISO 1183 |
| Molding Shrinkage | ASTM D955, ISO 294-4 | ||
| Flow : 24 hr | 0.74 | % | |
| Across Flow : 24 hr | 0.61 | % | |
| Water Absorption (24 hr, 50% RH) | 0.10 | % | ASTM D570 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 2650 | MPa | ASTM D638 |
| -- | 2630 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Yield | 22.8 | MPa | ASTM D638 |
| Break | 52.4 | MPa | ASTM D638 |
| Break | 54.9 | MPa | ISO 527-2 |
| Tensile Elongation | ASTM D638 | ||
| Yield | 1.9 | % | |
| Break | 5.9 | % | |
| Flexural Modulus | |||
| -- | 2600 | MPa | ASTM D790 |
| -- | 2730 | MPa | ISO 178 |
| Flexural Strength | |||
| -- | 96.5 | MPa | ASTM D790 |
| -- | 102 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 48 | J/m | ASTM D256 |
| 23°C 2 | 5.1 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | 1000 | J/m | ASTM D4812 |
| 23°C 3 | 80 | kJ/m² | ISO 180/1U |
| Instrumented Dart Impact | |||
| 23°C, Energy at Peak Load | 2.96 | J | ASTM D3763 |
| -- | 5.10 | J | ISO 6603-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed, 3.20 mm | 142 | °C | ASTM D648 |
| 0.45 MPa, Unannealed, 64.0 mm Span 4 | 130 | °C | ISO 75-2/Bf |
| 1.8 MPa, Unannealed, 3.20 mm | 135 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 64.0 mm Span 5 | 132 | °C | ISO 75-2/Af |
| CLTE | |||
| Flow : -40 to 40°C | 6.5E-5 | cm/cm/°C | ASTM E831 |
| Flow : -40 to 40°C | 6.1E-5 | cm/cm/°C | ISO 11359-2 |
| Transverse : -40 to 40°C | 6.1E-5 | cm/cm/°C | ASTM E831 |
| Transverse : -40 to 40°C | 6.2E-5 | cm/cm/°C | ISO 11359-2 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+2 to 1.0E+5 | ohms | ASTM D257 |
| Volume Resistivity | 1.0E+2 to 1.0E+5 | ohms·cm | ASTM D257 |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 80*10*4 |
| 3 . | 80*10*4 |
| 4 . | 80*10*4 mm |
| 5 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SUPREME Specialty PS SP564 | Supreme Petrochem Ltd. | PS (IRPS) | SUPREME Specialty PS |
| WELLAMID Nylon 6600 HWUVCP | CP-Polymer-Technik GmbH & Co. KG | Nylon 66 | WELLAMID Nylon |
| Network Polymers PS CPS 80 1800 | Network Polymers, Inc. | PS (GPPS) | Network Polymers PS |
| KIBIPOL® PR-040G | CHI MEI CORPORATION | IIR | KIBIPOL® |
| Kumho SBR 1778K | Korea Kumho Petrochemical Co., Ltd. | SBR, Emulsion | Kumho SBR |