PRL PC/TP-GP1 is a Polycarbonate + Polyester (PC+Polyester) product. It can be processed by injection molding and is available in North America. Characteristics include:
|
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| RoHS Compliance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.22 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (265°C/2.16 kg) | 5.0 to 15 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow (3.18 mm) | 0.50 to 0.80 | % | ASTM D955 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 120 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | ASTM D638 | ||
| Yield, 3.18 mm | 55.2 | MPa | |
| Break, 3.18 mm | 54.5 | MPa | |
| Tensile Elongation (Break, 3.18 mm) | 120 | % | ASTM D638 |
| Flexural Modulus (3.18 mm) | 2170 | MPa | ASTM D790 |
| Flexural Strength (3.18 mm) | 86.2 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 3.18 mm) | 800 | J/m | ASTM D256 |
| Gardner Impact (3.18 mm) | > 36.2 | J | ASTM D3029 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed, 3.18 mm | 121 | °C | |
| 1.8 MPa, Unannealed, 3.18 mm | 110 | °C |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 104 to 110 | °C | |
| Drying Time | 4.0 to 6.0 | hr | |
| Drying Time, Maximum | 8.0 | hr | |
| Rear Temperature | 249 to 271 | °C | |
| Middle Temperature | 254 to 277 | °C | |
| Front Temperature | 260 to 282 | °C | |
| Processing (Melt) Temp | 246 to 274 | °C | |
| Mold Temperature | 65.6 to 87.8 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Maxelast® P3940CH | Nantong Polymax Elastomer Technology, Co., Ltd | TPE | Maxelast® |
| ALCUDIA® EVA PA-441-S | REPSOL | EVA | ALCUDIA® EVA |
| HiFill® PA6 GB20 L | Techmer Engineered Solutions | Nylon 6 | HiFill® |
| LNP™ LUBRICOMP™ RFL34 compound | SABIC Innovative Plastics | Nylon 66 | LNP™ LUBRICOMP™ |
| Lotader® AX 8900 | Arkema | EMAAA | Lotader® |