EcoPaXX® Q-HG10
| Category: | Nylon 410 , Polyamide 410 |
| Manufacturer: | DSM Engineering Plastics |
| Trademark: | EcoPaXX® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | C9rrAG_EcoPaXX-Q-HG10.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
EcoPaXX® Q-HG10 is a Polyamide 410 (Nylon 410) material filled with 50% glass fiber. It is available in Asia Pacific, Europe, or North America. Important attributes of EcoPaXX® Q-HG10 are:
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Forms |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.52 | -- | g/cm³ | ISO 1183 |
| Molding Shrinkage | ISO 294-4 | |||
| Across Flow | 0.80 | -- | % | |
| Flow | 0.40 | -- | % | |
| Water Absorption (Equilibrium, 23°C, 50% RH) | 1.1 | -- | % | ISO 62 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | 16000 | 12000 | MPa | ISO 527-2 |
| Tensile Stress (Break) | 220 | 170 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 3.0 | 3.5 | % | ISO 527-2 |
| Flexural Modulus | 14600 | 11300 | MPa | ISO 178 |
| Flexural Stress | 335 | 250 | MPa | ISO 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | |||
| -30°C | 12 | -- | kJ/m² | |
| 23°C | 15 | 19 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179/1eU | |||
| -30°C | 80 | -- | kJ/m² | |
| 23°C | 80 | 85 | kJ/m² |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature | ||||
| 0.45 MPa, Unannealed | 245 | -- | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 215 | -- | °C | ISO 75-2/A |
| Melting Temperature 1 | 250 | -- | °C | ISO 11357-3 |
| CLTE | ISO 11359-2 | |||
| Flow | 4.2E-5 | -- | cm/cm/°C | |
| Transverse | 5.0E-5 | -- | cm/cm/°C |
| Additional Information | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Biobased Content - Carbon | 70 | -- | % | ASTM D6866 |
| Injection | Dry | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 4.0 to 8.0 | hr | |
| Rear Temperature | 250 to 270 | °C | |
| Middle Temperature | 260 to 280 | °C | |
| Front Temperature | 270 to 290 | °C | |
| Nozzle Temperature | 270 to 300 | °C | |
| Processing (Melt) Temp | 275 to 310 | °C | |
| Mold Temperature | 80.0 to 140 | °C | |
| Injection Rate | Moderate-Fast | ||
| Back Pressure | 3.00 to 10.0 | MPa | |
| Screw Compression Ratio | 2.5:1.0 |
| Note Message | |
|---|---|
| 1 . | 10°C/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Tenac™-C 3513 | Asahi Kasei Chemicals Corporation | Acetal (POM) Copolymer | Tenac™-C |
| New-prene™ 8680N | Total Polymer Vision (Suzhou) Co., LTD | PP+EPDM | New-prene™ |
| Evermore PUR SS-1335N | Evermore Chemical Industry Co., Ltd. | PUR, Unspecified | Evermore PUR |
| Kynar Flex® 2850 Black | Arkema | PVDF | Kynar Flex® |
| Pemex PX 20020 P | Pemex Petroquímica | LDPE | Pemex |