RIALGLASS H 07 S 50 G
| Category: | PP Homopolymer , Polypropylene Homopolymer |
| Manufacturer: | RIALTI Srl |
| Trademark: | RIALGLASS |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | C8osLY_RIALGLASS-H-07-S-50-G.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Polypropylene homopolymer 50% reinforced with glass fiber chemically coupled; heat stabilized; thermal and mechanical properties conspicuous in a wide temperature interval; low coefficient of linear thermal dilatation (from 30°C to 70°C) Medium flowabilty, compound indicated for injection molding of particulars with high stiffness and mechanical tightness in temperature, availble in natural version and colored as per sample. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.34 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 6.0 | g/10 min | ISO 1133 |
| Molding Shrinkage | ISO 294-4 | ||
| Across Flow | 0.75 | % | |
| Flow | 0.15 | % | |
| Water Absorption 1(23°C, 24 hr) | 0.020 | % | ISO 62 |
| Ash Content | 50 | % | ISO 3451 |
| Aging | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Accelerated Oven Aging (150°C) | 6.3 | day | ISO 4577 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness (Shore D, 15 sec) | 85 | ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | ISO 527-2/20 | ||
| Yield, 23°C | 105 | MPa | |
| Break, 23°C | 105 | MPa | |
| Tensile Strain | ISO 527-2/20 | ||
| Yield, 23°C | 1.5 | % | |
| Break, 23°C | 1.5 | % | |
| Flexural Modulus 2(23°C) | 11000 | MPa | ISO 178 |
| Flexural Stress (23°C) | 178 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Unnotched Impact Strength (23°C) | 45 | kJ/m² | ISO 179/1eU |
| Notched Izod Impact Strength | ISO 180/1A | ||
| -40°C | 9.0 | kJ/m² | |
| -20°C | 9.5 | kJ/m² | |
| 23°C | 10 | kJ/m² |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 165 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 155 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 145 | °C | ISO 306/B50 |
| Ball Pressure Test (145°C) | Pass | IEC 335 | |
| CLTE - Flow | 3.5E-5 | cm/cm/°C | ISO 11359-2 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (1.50 mm) | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 90.0 | °C | |
| Drying Time | 3.0 | hr | |
| Processing (Melt) Temp | 240 to 250 | °C | |
| Mold Temperature | 50.0 to 60.0 | °C | |
| Injection Rate | Fast |
| Note Message | |
|---|---|
| 1 . | 50%RH |
| 2 . | 2.0 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TAIRISAN NF2100 | Formosa Plastics Corporation | SAN | TAIRISAN |
| TEREZ PA 6 7851 T GF 30 H UV | TER HELL PLASTIC GMBH | Nylon 6 | TEREZ PA 6 |
| Kepamid® 2300ST | Korea Engineering Plastics Co., Ltd | Nylon 66 | Kepamid® |
| KumhoSunny PBT/ASA HBA5820G | Shanghai KumhoSunny Plastics Co., Ltd. | PBT+ASA | KumhoSunny PBT/ASA |
| Tunhe PET TH103 | Xinjiang Blueridge Tunhe Chemical Industry Co.,Ltd | PET | Tunhe PET |