LNP™ LUBRICOMP™ MAP41XXP compound
| Category: | PP, Unspecified , Polypropylene |
| Manufacturer: | SABIC Innovative Plastics Europe |
| Trademark: | LNP™ LUBRICOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | C8neIb_LNP-LUBRICOMP-MAP41XXP-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP* LUBRICOMP* MAP41XXP is a compound based on Polypropylene resin containing Aramid, PTFE and Silicone. Added Features include: Internally Lubricated. Also known as: LNP* LUBRICOMP* Compound MAL-4541 HP Product reorder name: MAP41XXP |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.02 | g/cm³ | ISO 1183 |
| Molding Shrinkage - Flow | 1.5 to 2.0 | % | Internal Method |
| Water Absorption (23°C, 24 hr) | 0.020 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 1400 | MPa | ISO 527-2/1 |
| Tensile Stress | ISO 527-2/50 | ||
| Yield | 25.0 | MPa | |
| Break | 18.0 | MPa | |
| Tensile Strain | ISO 527-2/50 | ||
| Yield | 5.9 | % | |
| Break | 56 | % | |
| Flexural Modulus 1 | 1400 | MPa | ISO 178 |
| Flexural Stress 2 | ISO 178 | ||
| -- 3 | 32.0 | MPa | |
| -- 4 | 37.0 | MPa | |
| Coefficient of Friction (vs. Itself - Dynamic) | 0.33 | ASTM D3702 Modified | |
| Wear Factor - Washer | 4.00 | 10^-10 in^5-min/ft-lb-hr | ASTM D3702 Modified |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact Strength 5(23°C) | 4.0 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact Strength 6(23°C) | 25 | kJ/m² | ISO 180/1U |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature 7 | |||
| 0.45 MPa, Unannealed, 64.0 mm Span | 100 | °C | ISO 75-2/Bf |
| 1.8 MPa, Unannealed, 64.0 mm Span | 64.0 | °C | ISO 75-2/Af |
| CLTE | ISO 11359-2 | ||
| Flow : 23 to 60°C | 1.6E-4 | cm/cm/°C | |
| Transverse : 23 to 60°C | 1.3E-4 | cm/cm/°C |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 | °C | |
| Drying Time | 4.0 | hr | |
| Rear Temperature | 193 to 204 | °C | |
| Middle Temperature | 199 to 210 | °C | |
| Front Temperature | 204 to 216 | °C | |
| Processing (Melt) Temp | 216 to 221 | °C | |
| Mold Temperature | 32.2 to 48.9 | °C | |
| Back Pressure | 0.172 to 0.344 | MPa | |
| Screw Speed | 30 to 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | 2.0 mm/min |
| 3 . | Yield |
| 4 . | Break |
| 5 . | 80*10*4 |
| 6 . | 80*10*4 |
| 7 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| PRL PPX-FRG30 | Polymer Resources Ltd. | PPE+PS | PRL |
| S&E PVC GA-3028 | S&E Specialty Polymers, LLC | PVC, Unspecified | S&E PVC |
| Sylvin 8828-74 Natural | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| Kepital® F20-03 BBK | KEP Americas | Acetal (POM) Copolymer | Kepital® |
| Braskem PE GM5255 | Braskem | HDPE | Braskem PE |