VENYL SW300 - 8229
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | AD majoris |
| Trademark: | VENYL |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | C8gSvw_VENYL-SW300---8229.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
VENYL SW300 - 8229 is a 30% glass bead filled polyamide 6 intended for Injection moulding. APPLICATIONS VENYL SW300 - 8229 has been developed especially for very demanding applications in automotive industry and electrical parts. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.37 | -- | g/cm³ | ISO 1183 |
| Molding Shrinkage | 0.70 to 1.2 | -- | % | |
| Water Absorption (Equilibrium, 23°C, 50% RH) | 2.0 | -- | % |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | 3900 | 1200 | MPa | ISO 527-2 |
| Tensile Stress (Break) | 75.0 | 40.0 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 10 | 30 | % | ISO 527-2 |
| Flexural Modulus | 3600 | 1100 | MPa | ISO 178 |
| Flexural Stress | 140 | 65.0 | MPa | ISO 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | 4.5 | 12 | kJ/m² | ISO 179 |
| Charpy Unnotched Impact Strength | 70 kJ/m² | No Break | ISO 179 |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature | ||||
| 0.45 MPa, Unannealed | 190 | -- | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 180 | -- | °C | ISO 75-2/A |
| Melting Temperature (DSC) | 220 | -- | °C | ISO 3146 |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Volume Resistivity | 1.0E+14 | 1.0E+12 | ohms·cm | DIN 53482 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flame Rating (1.60 mm) | HB | -- | UL 94 |
| Injection | Dry | Unit | |
|---|---|---|---|
| Rear Temperature | 265 to 280 | °C | |
| Middle Temperature | 255 to 270 | °C | |
| Front Temperature | 255 to 270 | °C | |
| Nozzle Temperature | 240 to 275 | °C | |
| Mold Temperature | 60.0 to 100 | °C | |
| Injection Pressure | 60.0 to 90.0 | MPa | |
| Injection Rate | Fast | ||
| Holding Pressure | 50.0 to 70.0 | MPa | |
| Screw L/D Ratio | 15.0:1.0 to 20.0:1.0 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| NYLOY® MG-0033N-V0 HG35N4 | Nytex Composites Co., Ltd. | Nylon, Unspecified | NYLOY® |
| ELASTOSIL® N 9111 BLACK | Wacker Chemie AG | Silicone | ELASTOSIL® N |
| Hax™ HFX 500 | Fainplast Compounds S.r.l | Polyolefin, Unspecified | Hax™ |
| LNP™ LUBRICOMP™ SFP36 compound | SABIC Innovative Plastics | Nylon 12 | LNP™ LUBRICOMP™ |
| Monprene® RG-17280 (PRELIMINARY DATA) | Teknor Apex Company | TPE | Monprene® |