SABIC® HDPE B5403
| Category: | HDPE , High Density Polyethylene |
| Manufacturer: | Saudi Basic Industries Corporation (SABIC) |
| Trademark: | SABIC® HDPE |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | C858Ud_SABICHDPEB5403.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
SABIC® HDPE B5403 is typically used for blow moulding UN certified Tight Head drums, from 25 up to 220 liter. This food approved grade combines good processing performance with good stress crack resistance, stiffness and impact performance. This product is not intended for and must not be used in any pharmaceutical/medical applications. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.954 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) | ISO 1133 | ||
| 190°C/21.6 kg | 2.7 | g/10 min | ISO 1133 |
| 190°C/5.0 kg | 0.10 | g/10 min | ISO 1133 |
| Environmental Stress-Cracking Resistance (10% Igepal CO-630, Compression Molded, F50) | 170 | hr | ASTM D1693B |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D, Compression Molded) | 61 | ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (2.00 mm, Compression Molded) | 1250 | MPa | ISO 527-2/1BA/50 |
| Tensile Stress | ISO 527-2/1BA/50 | ||
| Yield, 2.00mm, molded | 26.0 | MPa | ISO 527-2/1BA/50 |
| Fracture, 2.00mm, molded | 39.0 | MPa | ISO 527-2/1BA/50 |
| Tensile Strain | ISO 527-2/1BA/50 | ||
| Yield, 2.00mm, molded | 14 | % | ISO 527-2/1BA/50 |
| Fracture, 2.00mm, molded | > 1000 | % | ISO 527-2/1BA/50 |
| Flexural Modulus (2.00 mm, Compression Molded) | 1250 | MPa | ISO 178 |
| Flexural Stress (2.00 mm, Compression Molded) | 27.0 | MPa | ISO 178 |
| ESCR (Strain Hardening) - Gp | 23.0 | MPa | ISO 18488 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Enthalpy Change | 195 | J/g | ISO 11357-3 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | ISO 180/A | ||
| -30°C, molded | 60 | kJ/m² | ISO 180/A |
| 23°C, molded | 72 | kJ/m² | ISO 180/A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (0.45 MPa, Unannealed) | 78.0 | °C | ISO 75-2/B |
| Vicat Softening Temperature | 129 | °C | ISO 306/A |
| Melting Temperature (DSC) | 132 | °C | ISO 11357-3 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TRANSMARE® 14CT30-0.002 | Transmare Compounding B.V. | PP Copolymer | TRANSMARE® |
| Witcom PPS 6C/3L1-L | Witcom Engineering Plastics B.V. | PPS | Witcom PPS |
| POLIMAXX 1126NK | IRPC Public Company Limited | PP Homopolymer | POLIMAXX |
| Softell TKG 300N C11498 | LyondellBasell Industries | PP Copolymer | Softell |
| Hostacom TRC 333N D72645 | LyondellBasell Industries | PP Copolymer | Hostacom |