KumhoSunny PBT/ASA HBA5820G
| Category: | PBT+ASA , Polybutylene Terephthalate + ASA |
| Manufacturer: | Shanghai KumhoSunny Plastics Co., Ltd. |
| Trademark: | KumhoSunny PBT/ASA |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | C7wBQm_KumhoSunny-PBT-ASA-HBA5820G.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| HBA5820G is a 20% glass reinforced PBT/ASA blend with excellent mechanical properties, high dimensional stability and low density. Applications: connectors and automotive industry. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| UL File Number |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density (23°C) | 1.38 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (265°C/2.16 kg) | 16 | g/10 min | ISO 1133 |
| Molding Shrinkage (23°C) | 0.40 to 0.80 | % | ISO 294-4 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | 95.0 | MPa | ISO 527-2/5 |
| Tensile Strain (Break) | 2.0 | % | ISO 527-2/5 |
| Flexural Modulus 1 | 6000 | MPa | ISO 178 |
| Flexural Stress 2 | 135 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179 | ||
| -30°C | 4.0 | kJ/m² | |
| 23°C | 8.0 | kJ/m² | |
| Charpy Unnotched Impact Strength (23°C) | 40 | kJ/m² | ISO 179 |
| Notched Izod Impact Strength (23°C) | 8.0 | kJ/m² | ISO 180 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature 3(0.45 MPa, Unannealed) | 180 | °C | ISO 75-2/B |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | > 1.0E+15 | ohms | IEC 60093 |
| Volume Resistivity | > 1.0E+15 | ohms·cm | IEC 60093 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 100 to 120 | °C | |
| Drying Time | 4.0 to 6.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Rear Temperature | 235 to 240 | °C | |
| Middle Temperature | 240 to 260 | °C | |
| Front Temperature | 240 to 260 | °C | |
| Nozzle Temperature | 250 to 260 | °C | |
| Processing (Melt) Temp | 245 to 260 | °C | |
| Mold Temperature | 50.0 to 80.0 | °C | |
| Back Pressure | 0.200 to 0.800 | MPa | |
| Screw Speed | 20 to 100 | rpm |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | 2.0 mm/min |
| 3 . | 120°C/h |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| PrimaFlex® CP 2003-BK | Plastic Solutions, Inc. | PP Impact Copolymer | PrimaFlex® |
| AKROMID® A3 GF 20 1 black (2307) | AKRO-PLASTIC GmbH | Nylon 66 | AKROMID® |
| Edgetek™ ET3500-5002 BK | PolyOne Corporation | ASA+PC | Edgetek™ |
| ENFLEX V1045A | ENPLAST Americas, a Ravago Group Company | TPV | ENFLEX |
| Hostacom PP 3100 10 | LyondellBasell Industries | PP Copolymer | Hostacom |