VAMPLEN 1028 V0
| Category: | PP Homopolymer , Polypropylene Homopolymer |
| Manufacturer: | Vamp Tech |
| Trademark: | VAMPLEN |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | C6lbvn_VAMPLEN-1028-V0.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| UL 94 V0 at 1,6 mm, homopolymer, 10% glass fiber, halogen free, RoHS. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| RoHS Compliance |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.11 | g/cm³ | ASTM D792 |
| Molding Shrinkage | ASTM D955 | ||
| Flow | 1.1 | % | |
| Across Flow | 1.1 | % | |
| Water Absorption (Saturation) | 0.020 | % | ASTM D570 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2000 | MPa | ASTM D638 |
| Tensile Strength (Yield) | 20.0 | MPa | ASTM D638 |
| Tensile Elongation (Break) | > 20 | % | ASTM D638 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact Strength | 2.2 | kJ/m² | ISO 180/A |
| Unnotched Izod Impact Strength | 18 | kJ/m² | ISO 180 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 70.0 | °C | ASTM D648A |
| Vicat Softening Temperature | 105 | °C | ASTM D1525 1 |
| RTI Elec | 110 | °C | UL 746 |
| RTI Imp | 110 | °C | UL 746 |
| RTI Str | 110 | °C | UL 746 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Comparative Tracking Index | 600 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 1.60 mm | V-0 | ||
| 3.20 mm | V-0 | ||
| Glow Wire Flammability Index (3.00 mm) | 850 | °C | IEC 60695-2-12 |
| Glow Wire Ignition Temperature (3.00 mm) | 775 | °C | IEC 60695-2-13 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 70.0 | °C | |
| Drying Time | 3.0 | hr | |
| Processing (Melt) Temp | 210 | °C | |
| Mold Temperature | 60.0 | °C |
| Note Message | |
|---|---|
| 1 . | Loading 2 (50 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Adflex KS021P | LyondellBasell Industries | TPO (POE) | Adflex |
| Borealis PP MD206U | Borealis AG | PP, Unspecified | Borealis PP |
| Ferro PP LPP20BN53HB | Ferro Corporation | PP, Unspecified | Ferro PP |
| Karina IVORY PVC COMPOUND ML-IS-SN-PO (*) | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| Luranyl® KR 2401 | ROMIRA GmbH | PPE+PS | Luranyl® |