SUSTAMID 6G PD 140
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | Röchling Sustaplast SE & Co. KG |
| Trademark: | SUSTAMID |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | C6lRgW_SUSTAMID-6G-PD-140.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
Product characteristics
Typical fields of application
|
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.14 | g/cm³ | ISO 1183 |
| Water Absorption (Equilibrium, 23°C, 50% RH) | 2.4 | % | ISO 62 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness (Shore D) | 81 | ISO 868 | |
| Ball Indentation Hardness | 164 | MPa | ISO 2039-1 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2900 | MPa | ISO 527-2 |
| Tensile Stress (Yield) | 70.0 | MPa | ISO 527-2 |
| Tensile Strain (Break) | > 50 | % | ISO 527-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 90.0 | °C | ISO 75-2/A |
| Continuous Use Temperature | |||
| -- 1 | -40.0 to 100 | °C | |
| -- 2 | < 160 | °C | |
| Melting Temperature | 210 | °C | ISO 11357-3 |
| CLTE - Flow | 8.0E-5 | cm/cm/°C | DIN 53752 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 3.00 mm | HB | ||
| 6.00 mm | HB |
| Note Message | |
|---|---|
| 1 . | Long Term |
| 2 . | Short Term |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Rotofoam® 93050 | Polimeros Mexicanos s.a. de c.v. | LMDPE | Rotofoam® |
| Teflon® PFA 940HP Plus | DuPont Fluoropolymers | PFA | Teflon® PFA |
| Aaroprene® TFIPP 2040 | Aaron Industries Corp. | PP, Unspecified | Aaroprene® |
| NYLEM® 6 GBR 15 | EMAS Plastik San.Tic.AS. | Nylon 6 | NYLEM® |
| LubriOne™ PS-30CF/15T BK701 | PolyOne Corporation | PBT | LubriOne™ |