Sinpolene TPP1040
| Category: | PP Homopolymer , Polypropylene Homopolymer |
| Manufacturer: | Teknor Apex Asia Pacific PTE. LTD. |
| Trademark: | Sinpolene |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | C6eIy2_Sinpolene-TPP1040.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Sinpolene TPP1040 is a Polypropylene Homopolymer (PP Homopolymer) material filled with 40% talc. It is available in Asia Pacific for injection molding. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.22 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 10 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow | 0.60 to 0.80 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Yield) | 28.0 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 15 | % | ASTM D638 |
| Flexural Modulus | 3200 | MPa | ASTM D790 |
| Flexural Strength | 50.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | 25 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (0.45 MPa, Unannealed) | 136 | °C | ASTM D648 |
| Vicat Softening Temperature | 154 | °C | ASTM D1525 1 |
| Note Message | |
|---|---|
| 1 . | Loading 1 (10 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Electrafil® J-1200/CF/20 NAT | Techmer Engineered Solutions | ABS | Electrafil® |
| Grivory® GV-2 FWA nat | EMS-GRIVORY | Nylon 66+Nylon 6I/X | Grivory® |
| KW Plastics KW 621-T30 | KW Plastics | PP Impact Copolymer | KW Plastics |
| IDI BMC Rosite 3550C | IDI Composites International | TS, Unspecified | IDI BMC |
| INTEGRAL™ 816 | The Dow Chemical Company | Polyolefin, Unspecified | INTEGRAL™ |