ADVANCENE™ EM-5333-AAH
| Category: | HDPE , High Density Polyethylene |
| Manufacturer: | ETHYDCO |
| Trademark: | ADVANCENE™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | C66gvu_ADVANCENEEM5333AAH.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
ADVANCENE™ EM-5333-AAH HDPE Resin is a multipurpose polymer designed for high speed production of blow molded containers used to package household industrial chemicals (e.g detergents, bleach, fabric softeners), toiletries and cosmetics (e.g shampoos, creams, lotions, etc.), health and medical aids, and food products. In addition, it can be blow molded into other thin-walled parts and houseware items, and can be extruded into profiles. Main Characteristics:
|
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.953 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) | ASTM D1238, ISO 1133 | ||
| 190°C/2.16 kg | 0.38 | g/10 min | ASTM D1238, ISO 1133 |
| 190°C/21.6 kg | 33 | g/10 min | ASTM D1238, ISO 1133 |
| Environmental Stress-Cracking Resistance (50°C, 100% Igepal, F50) | 80.0 | hr | ASTM D1693 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D) | 61 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | ASTM D638, ISO 527-2 | ||
| Yield | 26.9 | MPa | ASTM D638, ISO 527-2 |
| Fracture | 31.0 | MPa | ASTM D638, ISO 527-2 |
| Tensile Elongation | ASTM D638, ISO 527-2 | ||
| Yield | 7.0 | % | ASTM D638, ISO 527-2 |
| Fracture | 1000 | % | ASTM D638, ISO 527-2 |
| Flexural Modulus - 2% Secant | 1000 | MPa | ASTM D790B, ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Impact Strength | |||
| -- 1 | 168 | kJ/m² | ASTM D1822 |
| -- | 168 | kJ/m² | ISO 8256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (0.45 MPa, Unannealed) | 73.0 | °C | ASTM D648, ISO 75-2/B |
| Brittleness Temperature | < -76.0 | °C | ASTM D746, ISO 974 |
| Vicat Softening Temperature | 129 | °C | ASTM D1525, ISO 306 |
| Peak Melting Temperature | 131 | °C | ASTM D3418, ISO 3146 |
| Peak Crystallization Temperature (DSC) | 118 | °C | ASTM D3418, ISO 3146 |
| Note Message | |
|---|---|
| 1 . | Type S |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Maxelast® C4750 | Nantong Polymax Elastomer Technology, Co., Ltd | TPE | Maxelast® |
| MAXAMID™ EPDM666G33-BK09 | Pier One Polymers, Inc. | Nylon 66/6 | MAXAMID™ |
| Xuchuan XCW-30H | Xuchuan Chemical (Suzhou) Co., Ltd | PUR, Unspecified | Xuchuan |
| Dynaflex™ G7670-1 (Natural) | PolyOne Corporation | TPE | Dynaflex™ |
| LEXAN™ HPS1R resin | SABIC Innovative Plastics | PC | LEXAN™ |