Wellamid® MRGF30/10 42H-N
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | Wellman Engineering Resins |
| Trademark: | Wellamid® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | C3FcAN_Wellamid-MRGF30-10-42H-N.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Wellamid® MRGF30/10 42H-N is a Polyamide 6 (Nylon 6) material filled with 40% glass\mineral. It is available in Asia Pacific, Europe, Latin America, or North America for injection molding. Primary attribute of Wellamid® MRGF30/10 42H-N: Flame Rated. Typical application of Wellamid® MRGF30/10 42H-N: Automotive |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.46 | g/cm³ | ISO 1183 |
| Molding Shrinkage | ISO 294-4 | ||
| Across Flow : 23°C | 0.70 to 1.1 | % | |
| Flow : 23°C | 0.50 to 0.90 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (Yield, 23°C) | 105 | MPa | ISO 527-2 |
| Tensile Strain (Yield, 23°C) | 4.0 | % | ISO 527-2 |
| Flexural Modulus (23°C) | 6900 | MPa | ISO 178 |
| Flexural Stress (23°C) | 175 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact Strength (23°C) | 4.0 | kJ/m² | ISO 180 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 190 | °C | ISO 75-2/A |
| Melting Temperature (DSC) | 220 | °C | ISO 3146 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (0.750 mm) | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 79.4 | °C | |
| Drying Time | 2.0 to 4.0 | hr | |
| Suggested Max Moisture | 0.20 | % | |
| Rear Temperature | 277 to 293 | °C | |
| Middle Temperature | 271 to 282 | °C | |
| Front Temperature | 266 to 277 | °C | |
| Nozzle Temperature | 254 to 282 | °C | |
| Processing (Melt) Temp | 271 to 299 | °C | |
| Mold Temperature | 71.1 to 93.3 | °C | |
| Injection Pressure | 34.5 to 138 | MPa | |
| Back Pressure | 0.345 | MPa | |
| Screw Speed | 30 to 120 | rpm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Telcar® GS5071 | Teknor Apex Asia Pacific PTE. LTD. | TPE | Telcar® |
| ASI POLYPROPYLENE 984 | A. Schulman Inc. | PP Impact Copolymer | ASI POLYPROPYLENE |
| Lupol® LW4302 | LG Chem Ltd. | PP, Unspecified | Lupol® |
| Sylvin 7833-85 White 1574 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| Petrothene® GA818092 | LyondellBasell Industries | LLDPE | Petrothene® |