Kynar Flex® 3120-50
| Category: | PVDF , Polyvinylidene Fluoride |
| Manufacturer: | Arkema |
| Trademark: | Kynar Flex® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | C32fRq_Kynar-Flex-3120-50.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
KYNAR FLEX® 3120-50 is a pelletized semi-crystalline VF2 based copolymer. It can be molded or extruded and has a useful temperature range from -40°C - 150°C. KYNAR FLEX® 3120-50 has a UL RTI of 150°C KYNAR FLEX® 3121-50 can be used in compounding for wire and cable as well as other extrusion applications. KYNAR FLEX® 3121-50 is a specially designed powder used as a polymer process aid (PPA) for polyolefins. The use of KYNAR FLEX® 3120-50 or KYNAR FLEX 3121-50 at 200 - 1000 ppm levels reduces extruder pressure, improves surface finish, reduces die build up, and improves gauge control. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.76 to 1.79 | g/cm³ | ASTM D792 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D, 23°C) | 65 to 70 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | ASTM D638 | ||
| Yield, 23°C | 24.1 to 34.5 | MPa | |
| Break, 23°C | 34.5 to 48.3 | MPa | |
| Tensile Elongation (Break, 23°C) | 300 to 550 | % | ASTM D638 |
| Flexural Modulus (23°C) | 621 to 827 | MPa | ASTM D790 |
| Flexural Strength (23°C) | 20.7 to 34.5 | MPa | ASTM D790 |
| Compressive Strength (23°C) | 31.0 to 41.4 | MPa | ASTM D695 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Peak Melting Temperature | 161 to 168 | °C | ASTM D3418 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity 1(20°C) | 2.0E+14 | ohms·cm | ASTM D257 |
| Fill Analysis | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Melt Viscosity (232°C, 100 sec^-1) | 2000 to 2600 | Pa·s | ASTM D3835 |
| Note Message | |
|---|---|
| 1 . | 65% R.H. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| WELLAMID Nylon 6000 MR 209 HWCP | CP-Polymer-Technik GmbH & Co. KG | Nylon 6 | WELLAMID Nylon |
| ACCULOY™ PCS003L | ACLO Compounders Inc. | ASA+PC | ACCULOY™ |
| Lotrène® LLDPE Q1018H | QATOFIN Company Limited | LLDPE | Lotrène® LLDPE |
| CALIBRE™ 351-15 | Sumika Styron Polycarbonate Limited | PC | CALIBRE™ |
| LNP™ STAT-KON™ DD000P compound | SABIC Innovative Plastics | PC | LNP™ STAT-KON™ |