SABIC® PPcompound 8900
| Category: | PP, Unspecified , Polypropylene |
| Manufacturer: | Saudi Basic Industries Corporation (SABIC) |
| Trademark: | SABIC® PPcompound |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | C2tQss_SABIC-PPcompound-8900.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
SABIC® PPcompound 8900 is a mineral filled modified polypropylene. This material combines high flow with a very high stiffness and high impact, as well as a very low shrinkage and CLTE. The high stiffness and low CLTE makes the material suited for high demanding applications. Typical applications include automotive exterior parts such as large thin wall zero gap bumper designs and (offline painted) vertical body panels. It can be used in painted and unpainted applications with UV stabilization added on demand. SABIC® PPcompound 8900 is a designated automotive grade. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.08 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 20 | g/10 min | ISO 1133 |
| Molding Shrinkage (24 hr) | 0.60 | % | Internal Method |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness (Shore D, Injection Molded) | 67 | ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | ISO 527-2/5/50 | ||
| Yield, 3.20 mm, Injection Molded | 24.0 | MPa | |
| Break, 3.20 mm, Injection Molded | 15.0 | MPa | |
| Tensile Strain (Break, 3.20 mm, Injection Molded) | 50 | % | ISO 527-2/5/50 |
| Flexural Modulus 1(Injection Molded) | 2300 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C, Injection Molded) | No Break | ISO 179/1eA | |
| Notched Izod Impact Strength | ISO 180/4A | ||
| -20°C, Injection Molded | 3.5 | kJ/m² | |
| 0°C, Injection Molded | 7.0 | kJ/m² | |
| 23°C, Injection Molded | 30 | kJ/m² |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (0.45 MPa, Unannealed) | 130 | °C | ISO 75-2/B |
| CLTE - Flow | ASTM D696 | ||
| -30 to 30°C | 4.5E-5 | cm/cm/°C | |
| 23 to 80°C | 5.5E-5 | cm/cm/°C |
| Note Message | |
|---|---|
| 1 . | Method I (3 point load) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Multi-Flex® TEA A 6003 ACN1 | Multibase, A Dow Corning Company | TPE | Multi-Flex® TEA |
| Gallonprene® GP210-5502L | Shenzhen Sungallon Rubber & Plastic Corporation Limited | TPE | Gallonprene® |
| HiFill® HDPE TM10 | Techmer Engineered Solutions | HDPE | HiFill® |
| INEOS HDPE HP50-25-153 | INEOS Olefins & Polymers USA | HDPE Copolymer | INEOS HDPE |
| LUVOCOM® 70-9046 | LEHVOSS Group | PK | LUVOCOM® |