Generic PP Homopolymer - Wollastonite (CaSiO3)
| Category: | PP Homopolymer , Polypropylene Homopolymer |
| Manufacturer: | Generic |
| Trademark: | Generic |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | C2e5Y5_Generic-PP-Homopolymer---Wollastonite-CaSiO3-.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
This data represents typical values that have been calculated from all products classified as: Generic PP Homopolymer - Wollastonite (CaSiO3) This information is provided for comparative purposes only. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.958 to 1.25 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 6.0 to 21 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow (23°C) | 0.60 to 1.2 | % | ASTM D955 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (23°C) | 78 to 96 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C) | 1600 to 3640 | MPa | ASTM D638 |
| Tensile Strength | ASTM D638 | ||
| Yield, 23°C | 30.0 to 35.1 | MPa | |
| Break, 23°C | 23.0 to 30.0 | MPa | |
| Tensile Elongation | ASTM D638 | ||
| Yield, 23°C | 4.0 to 7.0 | % | |
| Break, 23°C | 10 to 20 | % | |
| Flexural Modulus (23°C) | 1590 to 4220 | MPa | ASTM D790 |
| Flexural Strength (23°C) | 41.7 to 42.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 28 to 45 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed | 106 to 130 | °C | |
| 1.8 MPa, Unannealed | 60.0 to 82.2 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| MarFlex® 5619 | Chevron Phillips Chemical Company LLC | LDPE | MarFlex® |
| RTP 2099 x 121825 E | RTP Company | Nylon, Unspecified | RTP |
| FORMULA P FIB 3620/L | Putsch Kunststoffe GmbH | PP, Unspecified | FORMULA P |
| ISPLEN® PM 360 AT | REPSOL | PP Homopolymer | ISPLEN® |
| Karina BLUE COLOR CONCENTRATE 06/174-FC-LMP | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |