Category: | ABS+PBT , Acrylonitrile Butadiene Styrene + PBT |
Manufacturer: | Nippon A&L Inc. |
Trademark: | TECHNIACE® |
Fillers: | - |
Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
Delivery Terms | FOB, CIF, DAP, DAT, DDP |
PDF: | C2NZuN_TECHNIACE-TB-1701.pdf ![]() |
PRICE: | Order Products email sales@su-jiao.com |
Message |
---|
TECHNIACE® TB-1701 is an Acrylonitrile Butadiene Styrene + PBT (ABS+PBT) material. It is available in Asia Pacific or North America for injection molding. |
General Information | |
---|---|
Forms |
|
Processing Method |
|
Physical | Nominal Value | Unit | Test Method |
---|---|---|---|
Density (23°C) | 1.11 | g/cm³ | ISO 1183 |
Melt Volume-Flow Rate (MVR) (240°C/10.0 kg) | 31.0 | cm³/10min | ISO 1133 |
Molding Shrinkage | 0.50 to 0.80 | % | Internal Method |
Hardness | Nominal Value | Unit | Test Method |
---|---|---|---|
Rockwell Hardness (R-Scale, 23°C) | 107 | ISO 2039-2 |
Mechanical | Nominal Value | Unit | Test Method |
---|---|---|---|
Tensile Stress (Yield, 23°C) | 39.0 | MPa | ISO 527-2 |
Flexural Modulus (23°C) | 1950 | MPa | ISO 178 |
Flexural Stress (23°C) | 63.0 | MPa | ISO 178 |
Impact | Nominal Value | Unit | Test Method |
---|---|---|---|
Charpy Notched Impact Strength (23°C) | 55 | kJ/m² | ISO 179 |
Thermal | Nominal Value | Unit | Test Method |
---|---|---|---|
Heat Deflection Temperature (1.8 MPa, Unannealed) | 74.0 | °C | ISO 75-2/A |
CLTE - Flow (23 to 80°C) | 9.5E-5 | cm/cm/°C | JIS K7197 |
Injection | Nominal Value | Unit | |
---|---|---|---|
Drying Temperature | 90.0 to 100 | °C | |
Drying Time | > 3.0 | hr | |
Rear Temperature | 230 to 270 | °C | |
Middle Temperature | 230 to 270 | °C | |
Front Temperature | 230 to 270 | °C | |
Mold Temperature | 40.0 to 80.0 | °C |
Resin Grade | Manufacturer | Category | Trademark |
---|---|---|---|
Wellamid® MR409 22H-NBK3 | Wellman Engineering Resins | Nylon 66 | Wellamid® |
DURACON® AW-01 | Polyplastics Co., Ltd. | Acetal (POM) Copolymer+PE | DURACON® |
Geon™ CPVC EC520 | PolyOne Corporation | CPVC | Geon™ CPVC |
LNP™ THERMOCOMP™ AF004L compound | SABIC Innovative Plastics | ABS | LNP™ THERMOCOMP™ |
PLEXIGLAS® Film White WF002 | Evonik Industries AG | Film, PMMA | PLEXIGLAS® Film |