Lion Idemitsu Composites PPS C-7010SG
| Category: | PPS , Polyphenylene Sulfide |
| Manufacturer: | Lion Idemitsu Composites Co., Ltd. |
| Trademark: | Lion Idemitsu Composites PPS |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | C1lOSl_Lion-Idemitsu-Composites-PPS-C-7010SG.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Lion Idemitsu Composites PPS C-7010SG is a Polyphenylene Sulfide (PPS) product filled with 70% carbon\mineral. It is available in Asia Pacific. Characteristics include:
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Appearance |
|
| Part Marking Code (ISO 11469) |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 2.51 | g/cm³ | ISO 1183 |
| Molding Shrinkage 1 | ISO 294-4 | ||
| Across Flow | 0.30 | % | |
| Flow | 0.20 | % | |
| Water Absorption (23°C, 24 hr) | 0.010 | % | ISO 62 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (M-Scale) | 104 | ISO 2039-2 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | 148 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 0.60 | % | ISO 527-2 |
| Flexural Modulus | 26900 | MPa | ISO 178 |
| Flexural Stress | 243 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Unnotched Impact Strength | 4.6 | kJ/m² | ISO 179 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 268 | °C | ISO 75-2/A |
| CLTE | ISO 11359-2 | ||
| Flow | 1.7E-5 | cm/cm/°C | |
| Transverse | 1.8E-5 | cm/cm/°C |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | < 1.0E+2 | ohms·cm | ASTM D257 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.50 mm) | V-0 | UL 94 |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flowability 2(1.00 mm) | 6.70 | cm | Internal Method |
| Note Message | |
|---|---|
| 1 . | Internal Method |
| 2 . | Thickness 1mm, Cylinder temperature 320°C, Injection pressure 100MPa, Mold temperature 135°C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Avantra® 8530B | PMC Group Polymer Products | PS (HIPS) | Avantra® |
| Epoxies, Ect. 20-2370 | Epoxies, Etc. | PUR, Unspecified | Epoxies, Ect. |
| Keldax® 6868 | DuPont Packaging & Industrial Polymers | Ethylene Copolymer | Keldax® |
| Hostaform® C 52021 LS | Celanese Corporation | PPS | Hostaform® |
| Sinvicomp SGH6009 | Teknor Apex Asia Pacific PTE. LTD. | PVC, Flexible | SINVICOMP |