PRL PPX-GP8
| Category: | PPE+PS , Polyphenylene Ether + PS |
| Manufacturer: | Polymer Resources Ltd. |
| Trademark: | PRL |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | C1Vcad_PRL-PPX-GP8.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
PRL PPX-GP8 is a Polyphenylene Ether + PS (PPE+PS) product. It can be processed by injection molding and is available in North America. Characteristics include:
|
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| RoHS Compliance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.04 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (250°C/11.6 kg) | 14 to 20 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow | 0.50 to 0.70 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | ASTM D638 | ||
| Yield, 3.18 mm | 44.8 | MPa | |
| Break, 3.18 mm | 44.8 | MPa | |
| Tensile Elongation (Break, 3.18 mm) | 50 | % | ASTM D638 |
| Flexural Modulus (3.18 mm) | 1970 | MPa | ASTM D790 |
| Flexural Strength (Break, 3.18 mm) | 68.9 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | ASTM D256 | ||
| -40°C, 3.18 mm | 190 | J/m | |
| 23°C, 3.18 mm | 370 | J/m | |
| Gardner Impact (3.18 mm) | 16.9 | J | ASTM D3029 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed, 3.18 mm | 116 | °C | |
| 1.8 MPa, Unannealed, 3.18 mm | 110 | °C |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 1.0E+16 | ohms·cm | ASTM D257 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 104 to 110 | °C | |
| Drying Time | 3.0 to 4.0 | hr | |
| Drying Time, Maximum | 8.0 | hr | |
| Rear Temperature | 243 to 293 | °C | |
| Middle Temperature | 254 to 299 | °C | |
| Front Temperature | 266 to 304 | °C | |
| Processing (Melt) Temp | 274 to 302 | °C | |
| Mold Temperature | 65.6 to 98.9 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| PRIMALENE WPP693QB | Southern Polymer, Inc. | LLDPE | PRIMALENE |
| Sylvin 9650-50 Clear | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| KOPA® KN333G45BL | Kolon Plastics, Inc. | Nylon 66 | KOPA® |
| Karina BLACK PVC COMPOUND 751-48/ 1-E-IS-LMP | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| NORYL GTX™ GTX951W resin | SABIC Innovative Plastics Asia Pacific | PPE+PS+Nylon | NORYL GTX™ |