Braskem PP CP 241
| Category: | PP Copolymer , Polypropylene Copolymer |
| Manufacturer: | Braskem |
| Trademark: | Braskem PP |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | C0R3T0_Braskem-PP-CP-241.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Description: CP 241 is a high melt flow rate heterophasic copolymer with special reology for general purpose. This product offers excellent processability, easy mould filling and productivity, with good stiffness/impact strength balance. Applications: Thin-walled parts; Twisted closures. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.900 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 20 | g/10 min | ASTM D1238, ISO 1133 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness | |||
| R-Scale, Injection Molded | 68 | ASTM D785 | |
| R-Scale | 68 | ISO 2039-2 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Yield, Injection Molded) | 22.0 | MPa | ASTM D638, ISO 527-2 |
| Tensile Elongation (Yield, Injection Molded) | 10 | % | ASTM D638, ISO 527-2 |
| Flexural Modulus - 1% Secant | |||
| Injection Molded | 950 | MPa | ASTM D790 |
| Injection Molded | 1050 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| -20°C, Injection Molded | 50 | J/m | ASTM D256 |
| 23°C, Injection Molded | 300 | J/m | ASTM D256 |
| -20°C, Injection Molded | 5.3 | kJ/m² | ISO 180 |
| 23°C, Injection Molded | 14 | kJ/m² | ISO 180 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed, Injection Molded | 85.0 | °C | ASTM D648 |
| 0.45 MPa, Unannealed | 85.0 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed, Injection Molded | 53.0 | °C | ASTM D648 |
| 1.8 MPa, Unannealed | 53.0 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 145 | °C | ISO 306/A, ASTM D1525 1 |
| Note Message | |
|---|---|
| 1 . | Loading 1 (10 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| NEXUS PP CPP25/NB | Nexus Resin Group, LLC. | PP Impact Copolymer | NEXUS PP |
| AT 520 | Celanese EVA Performance Polymers | LDPE | AT |
| EL-Lene™ H511W | SCG Chemicals Co., Ltd. | HDPE | EL-Lene™ |
| Huafon JF-S-AH7090 | Huafon Group Co., Ltd. | PUR, Unspecified | Huafon |
| POCAN® B 1505 000000 | LANXESS GmbH | PBT | POCAN® |