GELOY™ HRA222 resin
| Category: | ASA , Acrylonitrile Styrene Acrylate |
| Manufacturer: | SABIC Innovative Plastics Europe |
| Trademark: | GELOY™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | C0OiDW_GELOYHRA222resin.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| GELOY HRA222 is a multi-purpose, chlorine and bromine free flame retardant PC+ASA alloy for injection molding processes. Use for exterior/interior electrical applications requiring UV resistance. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.17 | g/cm³ | ISO 1183 |
| Melt Volume-Flow Rate (MVR) (260°C/2.16 kg) | 13.0 | cm³/10min | ISO 1133 |
| Water Absorption | ISO 62 | ||
| Saturated, 23°C | 0.60 | % | ISO 62 |
| Equilibrium, 23°C, 50% RH | 0.20 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2520 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Yield 1 | 63.0 | MPa | ASTM D638 |
| Fracture 2 | 56.0 | MPa | ASTM D638 |
| Fracture | 45.0 | MPa | ISO 527-2/50 |
| Tensile Elongation | |||
| Yield 3 | 4.2 | % | ASTM D638 |
| Yield 4 | 4.3 | % | ASTM D638 |
| Fracture 5 | > 100 | % | ASTM D638 |
| Fracture 6 | > 100 | % | ASTM D638 |
| Fracture | > 50 | % | ISO 527-2/5, ISO 527-2/50 |
| Flexural Modulus 7 | 2520 | MPa | ISO 178 |
| Flexural Stress | 93.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact 8 | ISO 180/1A | ||
| -30°C | 9.0 | kJ/m² | ISO 180/1A |
| 0°C | 12 | kJ/m² | ISO 180/1A |
| 23°C | 17 | kJ/m² | ISO 180/1A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature 9 | |||
| 0.45 MPa, unannealed, 100 mm span | 99.0 | °C | ISO 75-2/Be |
| 1.8 MPa, unannealed, 100 mm span | 88.0 | °C | ISO 75-2/Ae |
| Vicat Softening Temperature | |||
| -- | 111 | °C | ISO 306/A50 |
| -- | 102 | °C | ISO 306/B50 |
| -- | 104 | °C | ISO 306/B120 |
| Ball Pressure Test (75°C) | Pass | IEC 60695-10-2 | |
| CLTE - Flow (-30 to 80°C) | 6.9E-5 | cm/cm/°C | ISO 11359-2 |
| Note Message | |
|---|---|
| 1 . | Type 1, 50mm/min |
| 2 . | Type 1, 50mm/min |
| 3 . | Type 1, 5.0 mm/min |
| 4 . | Type 1, 50mm/min |
| 5 . | Type 1, 5.0 mm/min |
| 6 . | Type 1, 50mm/min |
| 7 . | 2.0 mm/min |
| 8 . | 80*10*4 |
| 9 . | 120*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Manner Flexible PVC M1265 | Manner Plastics, L.P. | PVC, Flexible | Manner Flexible PVC |
| Zhongfa PP ZF-T30 | Yuyao Zhongfa Engineering Plastics Co. Ltd. | PP, Unspecified | Zhongfa |
| AKROMID® C3 GF 50 1 black (4401) | AKRO-PLASTIC GmbH | Nylon 66/6 | AKROMID® |
| ISPLEN® PG 370 AT | REPSOL | PP Homopolymer | ISPLEN® |
| Plantic® R1 | Plantic Technologies Limited | Biodeg Polymers | Plantic® |