VERSIFY™ 3300
| Category: | TPO (POE) , Elastomer |
| Manufacturer: | The Dow Chemical Company |
| Trademark: | VERSIFY™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | BzpHka_VERSIFY-3300.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
VERSIFY™ 3300 Elastomer can be used for stretch cling, elastic film and as a blend component in thermoplastic elastomers and thermoplastic olefins. It is a particularly good choice for cast stretch film sealants. When used as cling additive the grade generates higher unstretched film cling levels and can be used in blends at lower addition levels than needed with VLDPE. It gives consistent performance in hot and cold conditions, retains its characteristics over extended periods and delivers lower noise levels. Complies with:
|
| General Information | |
|---|---|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.867 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 8.0 | g/10 min | ASTM D1238 |
| Total Crystallinity | 11 | % | Internal Method |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness 1 | ASTM D2240 | ||
| Shore A, Compression Molded | 85 | ||
| Shore D, Compression Molded | 31 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Break, Compression Molded) | 19.6 | MPa | ASTM D638 |
| Tensile Elongation 2(Break, Compression Molded) | 750 | % | ASTM D638 |
| Flexural Modulus - 1% Secant (Compression Molded) | 38.9 | MPa | ASTM D790 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Glass Transition Temperature | -27.0 | °C | Internal Method |
| Vicat Softening Temperature | 42.0 | °C | ASTM D1525 |
| Melting Temperature (DSC) | 62.0 | °C | Internal Method |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gardner Gloss | ASTM D523 | ||
| 20°, 1000 µm, Compression Molded | 107 | ||
| 60°, 1000 µm, Compression Molded | 126 | ||
| Haze (2000 µm, Injection Molded) | 4.0 | % | ASTM D1003 |
| Note Message | |
|---|---|
| 1 . | Hardness after 10 seconds. |
| 2 . | 50 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Manner Flexible PVC M6113 FR | Manner Plastics, L.P. | PVC, Flexible | Manner Flexible PVC |
| Bynel® 4033 | DuPont Packaging & Industrial Polymers | HDPE | Bynel® |
| ELIX™ ABS E211 LNS013 | ELIX Polymers, S. L. | ABS | ELIX™ ABS |
| Huafon JF-W-6020 | Huafon Group Co., Ltd. | PUR, Unspecified | Huafon |
| LEMALLOY® BX503A-1 | Mitsubishi Engineering-Plastics Corp | PPE+Nylon 6 | LEMALLOY® |