LNP™ LUBRICOMP™ UX06425 compound
| Category: | PPA , Polyphthalamide |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ LUBRICOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | BzmihK_LNP-LUBRICOMP-UX06425-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP LUBRICOMP UX06425 is a compound based on Polyphthalamide (PPA) containing 10% Glass Fiber, 10% PTFE. Added features of this material include: Wear Resistant, Hot Water Moldable and Heat Stabilized. Also known as: LNP* LUBRICOMP* Compound UFL-4022 A HS HW Product reorder name: UX06425 |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | ASTM D792 | ||
| -- | 1.34 | g/cm³ | |
| -- | 1.33 | g/cm³ | |
| Molding Shrinkage | ASTM D955 | ||
| Flow : 24 hr | 0.70 to 0.90 | % | |
| Across Flow : 24 hr | 1.0 to 3.0 | % | |
| Water Absorption | |||
| 24 hr, 50% RH | 0.31 | % | ASTM D570 |
| Equilibrium, 23°C, 50% RH | 0.50 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 6610 | MPa | ASTM D638 |
| -- | 6420 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Break 2 | 89.0 | MPa | ASTM D638 |
| Break | 85.0 | MPa | ISO 527-2/5 |
| Tensile Strain | |||
| Yield | 1.4 | % | ISO 527-2/5 |
| Break 3 | 1.5 | % | ASTM D638 |
| Break | 1.5 | % | ISO 527-2/5 |
| Flexural Modulus | |||
| 50.0 mm Span 4 | 5710 | MPa | ASTM D790 |
| -- 5 | 5450 | MPa | ISO 178 |
| Flexural Stress | |||
| -- | 126 | MPa | ISO 178 |
| Break, 50.0 mm Span 6 | 132 | MPa | ASTM D790 |
| Coefficient of Friction | ASTM D3702 Modified | ||
| vs. Itself - Dynamic | 0.36 | ||
| vs. Itself - Static | 0.37 | ||
| Wear Factor | ASTM D3702 Modified | ||
| Ring | 0.600 | 10^-10 in^5-min/ft-lb-hr | |
| Washer | 15.5 | 10^-10 in^5-min/ft-lb-hr |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Minimum Moisture Content | 0.030 | % |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 33 | J/m | ASTM D256 |
| 23°C 7 | 3.6 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | 200 | J/m | ASTM D4812 |
| 23°C 8 | 12 | kJ/m² | ISO 180/1U |
| Instrumented Dart Impact | |||
| 23°C, Total Energy | 3.70 | J | ASTM D3763 |
| -- | 1.20 | J | ISO 6603-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed, 3.20 mm | 293 | °C | ASTM D648 |
| 0.45 MPa, Unannealed, 64.0 mm Span 9 | 289 | °C | ISO 75-2/Bf |
| 1.8 MPa, Unannealed, 3.20 mm | 260 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 64.0 mm Span 10 | 254 | °C | ISO 75-2/Af |
| CLTE | ASTM D696 | ||
| Flow : -30 to 30°C | 4.1E-5 | cm/cm/°C | |
| Transverse : -30 to 30°C | 7.5E-5 | cm/cm/°C |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 120 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.060 | % | |
| Rear Temperature | 318 to 324 | °C | |
| Front Temperature | 327 to 332 | °C | |
| Processing (Melt) Temp | 329 to 343 | °C | |
| Mold Temperature | 65.0 to 93.0 | °C | |
| Back Pressure | 0.350 | MPa | |
| Screw Speed | 30 to 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | Type I, 5.0 mm/min |
| 3 . | Type I, 5.0 mm/min |
| 4 . | 1.3 mm/min |
| 5 . | 2.0 mm/min |
| 6 . | 1.3 mm/min |
| 7 . | 80*10*4 |
| 8 . | 80*10*4 |
| 9 . | 80*10*4 mm |
| 10 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Unichem 5311 | Colorite Polymers | PVC, Unspecified | Unichem |
| CYCOLOY™ CM8622 resin | SABIC Innovative Plastics Europe | PC+ABS | CYCOLOY™ |
| ESTAPROP KUR 1010 TG05 | Cossa Polimeri S.r.l. | PP Copolymer | ESTAPROP |
| Geon™ Vinyl Flexible XV 3450 | PolyOne Corporation | PVC, Flexible | Geon™ Vinyl Flexible |
| HiFill FR® PA4/6 GF15 FR HS L | Techmer Engineered Solutions | Nylon 46 | HiFill FR® |