XENOY™ 1760 resin
| Category: | PC+PBT , Polycarbonate + PBT |
| Manufacturer: | SABIC Innovative Plastics Asia Pacific |
| Trademark: | XENOY™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | BykKrC_XENOY1760resin.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| 11% Glass Reinforced PBT+PC alloy. Impact/chemical resistant. Excellent physical property retention in automotive exteriors. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.30 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Volume-Flow Rate (MVR) (265°C/5.0 kg) | 12.0 | cm³/10min | ISO 1133 |
| Molding Shrinkage | Internal method | ||
| Flow : 3.20mm | 0.40 - 0.60 | % | Internal method |
| Transverse flow : 3.20mm | 0.40 - 0.60 | % | Internal method |
| Water Absorption | ISO 62 | ||
| Saturated, 23°C | 0.50 | % | ISO 62 |
| Equilibrium, 23°C, 50% RH | 0.15 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 5330 | MPa | ASTM D638 |
| -- | 4950 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Yield 2 | 84.0 | MPa | ASTM D638 |
| Yield | 84.0 | MPa | ISO 527-2/5 |
| Fracture 3 | 84.0 | MPa | ASTM D638 |
| Fracture | 84.0 | MPa | ISO 527-2/5 |
| Tensile Elongation | |||
| Yield 4 | 3.0 | % | ASTM D638 |
| Yield | 3.0 | % | ISO 527-2/5 |
| Fracture 5 | 4.0 | % | ASTM D638 |
| Fracture | 2.0 | % | ISO 527-2/5 |
| Flexural Modulus | |||
| 50.0mm span 6 | 3910 | MPa | ASTM D790 |
| -- 7 | 4050 | MPa | ISO 178 |
| Flexural Stress | |||
| -- | 134 | MPa | ISO 178 |
| Yield, 50.0mm span 8 | 131 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength 9(23°C) | 16 | kJ/m² | ISO 179/1eA |
| Notched Izod Impact | |||
| -30°C | 85 | J/m | ASTM D256 |
| 23°C | 95 | J/m | ASTM D256 |
| -30°C 10 | 3.0 | kJ/m² | ISO 180/1A |
| 23°C 11 | 3.0 | kJ/m² | ISO 180/1A |
| Instrumented Dart Impact | ASTM D3763 | ||
| -30°C, Energy at Peak Load | 3.00 | J | ASTM D3763 |
| -30°C, Total Energy | 3.00 | J | ASTM D3763 |
| -20°C, Energy at Peak Load | 4.00 | J | ASTM D3763 |
| 23°C, Total Energy | 8.00 | J | ASTM D3763 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 1.8 MPa, unannealed, 6.40mm | 115 | °C | ASTM D648 |
| 1.8 MPa, unannealed, 64.0mm span 12 | 104 | °C | ISO 75-2/Af |
| Vicat Softening Temperature | |||
| -- | 121 | °C | ASTM D1525 13 |
| -- | 135 | °C | ISO 306/B50 |
| -- | 130 | °C | ISO 306/B120 |
| Linear thermal expansion coefficient | |||
| Flow : -40 to 40°C | 7.7E-5 | cm/cm/°C | ASTM E831, ISO 11359-2 |
| Flow : -40 to 95°C | 4.5E-5 | cm/cm/°C | ASTM E831 |
| Lateral : -40 to 40°C | 3.8E-5 | cm/cm/°C | ASTM E831, ISO 11359-2 |
| Lateral : -40 to 95°C | 7.4E-5 | cm/cm/°C | ASTM E831 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 110 | °C | |
| Drying Time | 4.0 - 6.0 | hr | |
| Drying Time, Maximum | 8.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Suggested Shot Size | 50 - 80 | % | |
| Rear Temperature | 249 - 271 | °C | |
| Middle Temperature | 254 - 277 | °C | |
| Front Temperature | 260 - 282 | °C | |
| Nozzle Temperature | 254 - 277 | °C | |
| Processing (Melt) Temp | 260 - 282 | °C | |
| Mold Temperature | 65.6 - 93.3 | °C | |
| Back Pressure | 0.345 - 0.552 | MPa | |
| Screw Speed | 50 - 80 | rpm | |
| Vent Depth | 0.013 - 0.020 | mm |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | Type 1, 5.0 mm/min |
| 3 . | Type 1, 5.0 mm/min |
| 4 . | Type 1, 5.0 mm/min |
| 5 . | Type 1, 5.0 mm/min |
| 6 . | 1.3 mm/min |
| 7 . | 2.0 mm/min |
| 8 . | 1.3 mm/min |
| 9 . | 80*10*4 sp=62mm |
| 10 . | 80*10*4 |
| 11 . | 80*10*4 |
| 12 . | 80*10*4 mm |
| 13 . | 标准 B (120°C/h), 载荷2 (50N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| tefabloc® TP SD 333 65A | Mitsubishi Chemical Performance Polymers, Inc. | TPE | tefabloc® |
| TECHNO ABS 150L | Techno Polymer Co, Ltd. | ABS | TECHNO ABS |
| ULTEM™ 4002 resin | SABIC Innovative Plastics | PEI | ULTEM™ |
| Globalene® PT231M | Lee Chang Yung Chemical Industry Corp. | PP, Unspecified | Globalene® |
| FUDOWLITE® F5636F | Fudow Co., Ltd. | Phenolic | FUDOWLITE® |