Tenac™ GA520
| Category: | Acetal (POM) Homopolymer , Acetal (POM) Homopolymer |
| Manufacturer: | Asahi Kasei Chemicals Corporation |
| Trademark: | Tenac™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | ByEvFw_Tenac-GA520.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Tenac™ GA520 is an Acetal (POM) Homopolymer product filled with glass fiber. It is available in Africa & Middle East, Asia Pacific, Europe, or North America. Applications of Tenac™ GA520 include engineering/industrial parts, automotive and housings. Characteristics include:
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.56 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 15 | g/10 min | ISO 1133 |
| Molding Shrinkage | Internal Method | ||
| Flow | 1.5 to 1.8 | % | |
| Across Flow | 1.0 to 1.3 | % | |
| Water Absorption (23°C, 24 hr, 50% RH) | 0.20 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness | ASTM D785 | ||
| M-Scale | 90 | ||
| R-Scale | 120 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 4300 | MPa | ISO 527-2 |
| Tensile Stress | |||
| Yield | 54.0 | MPa | ISO 527-2 |
| -- | 53.0 | MPa | ASTM D638 |
| Tensile Elongation | |||
| Break | 15 | % | ASTM D638 |
| Break | 10 | % | ISO 527-2 |
| Flexural Modulus | |||
| -- | 3930 | MPa | ASTM D790 |
| -- | 4100 | MPa | ISO 178 |
| Flexural Strength | 100 | MPa | ASTM D790 |
| Taber Abrasion Resistance | 23.0 | mg | ASTM D1044 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | 4.0 | kJ/m² | ISO 179 |
| Notched Izod Impact | 33 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed | 174 | °C | ASTM D648 |
| 0.45 MPa, Unannealed | 165 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 152 | °C | ASTM D648 |
| 1.8 MPa, Unannealed | 118 | °C | ISO 75-2/A |
| CLTE - Flow | 7.0E-5 | cm/cm/°C | ASTM D696, ISO 11359-2 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 0.710 mm | HB | ||
| 1.50 mm | HB |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| ACCUTECH™ HP0334W20L | ACLO Compounders Inc. | PP Homopolymer | ACCUTECH™ |
| Axiall PVC 10756 | Axiall Corporation | PVC, Flexible | Axiall PVC |
| Karina BLUE PVC COMPOUND 900D06/366-B-IS-BZ | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| Badaflex® TPU 85A 8046 EX | Bada AG | TPU, Unspecified | Badaflex® |
| Dryflex® V 90A101 | ELASTO | TPV | Dryflex® |