Plexiglas® Rnew® B522
| Category: | PLA+PMMA , Polylactic Acid + PMMA |
| Manufacturer: | Altuglas International of Arkema Inc. |
| Trademark: | Plexiglas® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | BxHhwM_Plexiglas-Rnew-B522.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Plexiglas® Rnew® B522 is a sustainable, biobased acrylic alloy that has high transparency and impact resistance properties. It is an impact modified thermoplastic acrylic resin formulated for injection molding and extrusion applications. It also has outstanding chemical resistance and melt flow properties that are much higher than traditional impact acrylics, including Plexiglas® DR®. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.19 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (230°C/3.8 kg) | 3.9 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow | 0.20 to 0.60 | % | ASTM D955 |
| Water Absorption (24 hr) | 0.30 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (M-Scale) | 77 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2340 | MPa | ASTM D638 |
| Tensile Strength (Break) | 49.6 | MPa | ASTM D638 |
| Flexural Modulus | 2200 | MPa | ASTM D790 |
| Flexural Strength (Yield) | 70.3 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 43 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load 1(0.45 MPa, Annealed) | 67.2 | °C | ASTM D648 |
| Vicat Softening Temperature | 76.1 | °C | ASTM D1525 2 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Refractive Index 3 | 1.480 | ASTM D542 | |
| Transmittance (3180 µm) | 86.0 | % | ASTM D1003 |
| Haze (3180 µm) | < 5.0 | % | ASTM D1003 |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| ASTM Classification | PMMA Unspecified | ASTM D788 | |
| Renewable Carbon Conent | 35 | % | ASTM D6866 |
| Note Message | |
|---|---|
| 1 . | Annealing cycle: 4hrs @ 131°F |
| 2 . | Rate A (50°C/h), Loading 1 (10 N) |
| 3 . | ND @ 72°F |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Maxelast® P2950T | Nantong Polymax Elastomer Technology, Co., Ltd | TPE | Maxelast® |
| RJM SN602 | RJM International, Inc. | Nylon 66 | RJM |
| TOTAL Polystyrene Compound 827 | TOTAL Refining & Chemicals | PS (IRPS) | TOTAL Polystyrene |
| CP PRYME® Nylon 66 NN100STHSL BK | Chase Plastics Services Inc. | Nylon 66 | CP PRYME® Nylon 66 |
| LUVOCOM® 20-0778 | Lehmann & Voss & Co. | PPA | LUVOCOM® |