Durethan® BG 30 X XF 000000
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | LANXESS GmbH |
| Trademark: | Durethan® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | BxGfpG_Durethan-BG-30-X-XF-000000.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| PA 6, 30 % glass fibers/glass spheres, injection molding, improved flowability, improved surface finish, low tendency to warp |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Processing Method |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density (23°C) | 1.32 | -- | g/cm³ | ISO 1183 |
| Molding Shrinkage | ISO 2577 | |||
| Across Flow : 260°C, 2.00 mm 1 | 0.75 | -- | % | |
| Across Flow : 120°C, 4 hr, 2.00 mm 2 | 0.15 | -- | % | |
| Flow : 260°C, 2.00 mm 3 | 0.60 | -- | % | |
| Flow : 120°C, 4 hr, 2.00 mm 4 | 0.10 | -- | % |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus (23°C) | 5200 | 2600 | MPa | ISO 527-2/1 |
| Tensile Stress (Break, 23°C) | 85.0 | 45.0 | MPa | ISO 527-2/5 |
| Tensile Strain (Break, 23°C) | 3.2 | 6.9 | % | ISO 527-2/5 |
| Flexural Modulus 5(23°C) | 5000 | 2500 | MPa | ISO 178/A |
| Flexural Stress | ISO 178/A | |||
| 3.5% Strain, 23°C | 135 | 65.0 | MPa | |
| 23°C 6 | 140 | 80.0 | MPa | |
| Flexural Strain at Flexural Strength 7(23°C) | 3.8 | 6.3 | % | ISO 178/A |
| Additional Information | Dry | Conditioned | Test Method | |
|---|---|---|---|---|
| ISO Shortname | PA 6, GR, 10-050, (GB+GF) 30 | -- | ISO 1874 |
| Injection | Dry | Unit | Test Method |
|---|---|---|---|
| Residual Moisture Content | 0.030 to 0.12 | % | Karl Fisher |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | |||
| -30°C | < 10 | < 10 | kJ/m² | |
| 23°C | < 10 | 10 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179/1eU | |||
| -30°C | 40 | 35 | kJ/m² | |
| 23°C | 50 | 55 | kJ/m² | |
| Notched Izod Impact Strength | ISO 180/1A | |||
| -30°C | < 10 | < 10 | kJ/m² | |
| 23°C | < 10 | 10 | kJ/m² | |
| Unnotched Izod Impact Strength | ISO 180/1U | |||
| -30°C | 35 | 30 | kJ/m² | |
| 23°C | 40 | 50 | kJ/m² |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature | ||||
| 0.45 MPa, Unannealed | 210 | -- | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 185 | -- | °C | ISO 75-2/A |
| Vicat Softening Temperature | 195 | -- | °C | ISO 306/B120 |
| Melting Temperature 8 | 220 | -- | °C | ISO 11357-3 |
| CLTE | ISO 11359-2 | |||
| Flow : 23 to 55°C | 4.0E-5 | -- | cm/cm/°C | |
| Transverse : 23 to 55°C | 1.1E-4 | -- | cm/cm/°C |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Comparative Tracking Index (CTI) | 475 | -- | V | UL 746 |
| Comparative Tracking Index (Solution A) | 475 | -- | V | IEC 60112 |
| Injection | Dry | Unit | Test Method |
|---|---|---|---|
| Drying Temperature - Dry Air Dryer | 80.0 | °C | |
| Drying Time - Dry Air Dryer | 2.0 to 6.0 | hr | |
| Processing (Melt) Temp | 250 to 290 | °C | |
| Mold Temperature | 80.0 to 100 | °C |
| Note Message | |
|---|---|
| 1 . | 60x60x2mm, 80°C MT, 600 bar |
| 2 . | 60x60x2mm |
| 3 . | 60x60x2mm, 80°C MT, 600 bar |
| 4 . | 60x60x2mm |
| 5 . | 2.0 mm/min |
| 6 . | 2.0 mm/min |
| 7 . | 2 mm/min |
| 8 . | 10°C/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| ADDILENE J 290 M20 F | ADDIPLAST | PP, Unspecified | ADDILENE |
| ENVIROPLAS® ENV11-NC720 | ENVIROPLAS®, Inc. | PC | ENVIROPLAS® |
| PLUSTEK PA100/PA100NT-N | Polyram Ram-On Industries | Nylon 66 | PLUSTEK |
| Bergamid™ A70 G15 H NC714 | PolyOne Corporation | Nylon 66 | Bergamid™ |
| Sylvin 7844-85C Natural | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |