Lupol® HI5302R
| Category: | PP, Unspecified , Polypropylene |
| Manufacturer: | LG Chem Ltd. |
| Trademark: | Lupol® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | BvH4Ra_Lupol-HI5302R.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Lupol®HI5302R is a polypropylene material,. This product is available in North America, Latin America, Europe or Asia Pacific. The processing method is injection molding. Lupol®The typical application fields of HI5302R are: automobile industry |
| General Information | |
|---|---|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.12 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (250°C/2.16 kg) | 21 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow | 1.0 - 1.2 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Yield) | 22.6 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 30 | % | ASTM D638 |
| Flexural Modulus | 2550 | MPa | ASTM D790 |
| Flexural Strength (Yield) | 34.3 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 69 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 84.0 | °C | ASTM D648 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 - 100 | °C | |
| Drying Time | 3.0 - 4.0 | hr | |
| Hopper Temperature | 50.0 - 58.0 | °C | |
| Rear Temperature | 190 - 210 | °C | |
| Middle Temperature | 208 - 222 | °C | |
| Front Temperature | 211 - 228 | °C | |
| Nozzle Temperature | 205 - 220 | °C | |
| Mold Temperature | 50.0 - 58.0 | °C | |
| Injection Pressure | 2.94 - 11.8 | MPa | |
| Injection Rate | Fast | ||
| Back Pressure | 1.47 - 5.88 | MPa | |
| Screw Speed | 40 - 60 | rpm |
| Injection instructions |
|---|
| Secondary Injection Pressure: 20 to 100 kg/cm² |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TRAMID® 4110G33 | Samyang Corporation | Nylon, Unspecified | TRAMID® |
| Celanex® 7716 | Celanese Corporation | PBT | Celanex® |
| Flontech® FT-CAR33-GR2-1 | Guarniflon S.p.A. - Flontech Division | PTFE | Flontech® |
| Gallonprene® GP210-8511 | Shenzhen Sungallon Rubber & Plastic Corporation Limited | TPE | Gallonprene® |
| Plaslube® J-1/20/TF/20 NAT | Techmer Engineered Solutions | Nylon 66 | Plaslube® |