HiFill® PA6/6 GF60 IM HS L
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | Techmer Engineered Solutions |
| Trademark: | HiFill® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | ButKdT_HiFill-PA6-6-GF60-IM-HS-L.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
HiFill®PA6/6 GF60 IM HS L is a polyamide 66 (nylon 66) product, which contains a 60% glass fiber reinforced material. It can be processed by injection molding and is available in North America. Features include:
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Specific Gravity | 1.67 | -- | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow (3.18 mm) | 0.20 | -- | % | ASTM D955 |
| Water Absorption (24 hr) | 0.45 | -- | % | ASTM D570 |
| Hardness | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Rockwell Hardness (R-Scale) | 121 | -- | ASTM D785 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Strength (Break) | 186 | 159 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 3.0 | 4.0 | % | ASTM D638 |
| Flexural Modulus | 14500 | 11700 | MPa | ASTM D790 |
| Flexural Strength | 276 | 241 | MPa | ASTM D790 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Notched Izod Impact (23°C, 3.18 mm) | 370 | 430 | J/m | ASTM D256 |
| Unnotched Izod Impact (3.18 mm) | No Break | No Break | ASTM D256 |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 257 | -- | °C | ASTM D648 |
| CLTE - Flow | 2.3E-5 | -- | cm/cm/°C | ASTM D696 |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Surface Resistivity | 1.0E+11 | -- | ohms | ASTM D257 |
| Volume Resistivity | 1.0E+9 | -- | ohms·cm | ASTM D257 |
| Dielectric Strength 1 | 20 | -- | kV/mm | ASTM D149 |
| Additional Information | Dry | Conditioned | ||
|---|---|---|---|---|
| TPCI # | 8874101 | -- |
| Injection | Dry | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 | °C | |
| Drying Time | 2.0 - 4.0 | hr | |
| Suggested Max Moisture | 0.12 | % | |
| Rear Temperature | 282 - 293 | °C | |
| Middle Temperature | 288 - 299 | °C | |
| Front Temperature | 277 - 288 | °C | |
| Nozzle Temperature | 282 - 293 | °C | |
| Processing (Melt) Temp | 282 - 304 | °C | |
| Mold Temperature | 54.4 - 93.3 | °C | |
| Injection Rate | Moderate-Fast | ||
| Back Pressure | 0.345 - 0.689 | MPa |
| Injection instructions |
|---|
| Screw Speed: MediumRecommendations for Molding and Tool Conditions: Well ventedMoisture Content, as received: Product is packaged at 0.2% or less.Recomended Max Moisture: 0.12% down to 0.08% |
| Note Message | |
|---|---|
| 1 . | Method A (short time) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Nylene® 9643 | Custom Resins Group | Nylon 66/6 | Nylene® |
| ALTECH® PA6 A 2045/100 GF45 | ALBIS PLASTIC GmbH | Nylon 6 | ALTECH® PA6 |
| LNP™ THERMOCOMP™ RZ006SXP compound | SABIC Innovative Plastics | Nylon 66 | LNP™ THERMOCOMP™ |
| LNP™ THERMOCOMP™ Lexan_LGK3020 compound | SABIC Innovative Plastics | PC | LNP™ THERMOCOMP™ |
| PENTAMID B GV10 GK20 H RC schwarz | PENTAC Polymer GmbH | Nylon 6 | PENTAMID B |