NYCOA Polyamide 2137
| Category: | Nylon Copolymer , Polyamide Copolymer |
| Manufacturer: | Nycoa (Nylon Corporation of America) |
| Trademark: | NYCOA Polyamide |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | BtGk3T_NYCOA-Polyamide-2137.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
NYCOA 2137 is low viscosity Nylon copolymer resin that exhibits excellent transparency. The resin was developed especially for applications requiring transparency in thickness up to 5 mm, while retaining the properties and chemical resistance inherent to nylon 6. NYCOA 2137 has been specifically designed to offer easy processability. It can be processed on conventional injection equipment designed to process standard grades of nylon. NYCOA 2137 is available with custom additive packages: heat stabilizer and/or UV stabilizer. Typical injection molding applications include sight glasses, chemical splash goggles, fashion eyeglass frame, high-voltage switch casings, filter housings, pump casings, flow meters, liquid-level indicators, and filter bowls for gas. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.11 | g/cm³ | ASTM D792 |
| Molding Shrinkage | ASTM D955 | ||
| Flow | 1.0 | % | ASTM D955 |
| Transverse flow | 1.2 | % | ASTM D955 |
| Water Absorption (24 hr) | 1.7 | % | ASTM D570 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1 | 75.0 | MPa | ASTM D638 |
| Tensile Elongation 2(Break) | 50 | % | ASTM D638 |
| Flexural Modulus 3 | 2170 | MPa | ASTM D790 |
| Flexural Strength 4 | 84.8 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (6.35 mm) | 69 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Melting Temperature | 199 | °C | DSC |
| Additional Information |
|---|
| The value listed as Melting Point DSC, was tested in accordance with ASTM D789. |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 71.1 | °C | |
| Drying Time | 4.0 - 6.0 | hr | |
| Rear Temperature | 204 - 216 | °C | |
| Middle Temperature | 216 - 227 | °C | |
| Front Temperature | 221 - 232 | °C | |
| Nozzle Temperature | 221 - 238 | °C | |
| Processing (Melt) Temp | 216 - 232 | °C | |
| Mold Temperature | 4.44 - 10.0 | °C | |
| Injection Rate | Fast | ||
| Back Pressure | 0.138 - 0.345 | MPa | |
| Cushion | 1.59 - 6.35 | mm | |
| Screw L/D Ratio | 18.0:1.0 | ||
| Screw Compression Ratio | 2.5:1.0 |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 50 mm/min |
| 3 . | 50 mm/min |
| 4 . | 50 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Polymer-E EV305 | Asia Polymer Corporation (APC) | EVA | Polymer-E |
| Retpol® 7839/4 HS UV2 | PolyPacific Pty. Ltd. | PP, Unspecified | Retpol® |
| Sylvin 5132-75 Black | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| TUFNYL® RXXIC BLUE | SRF Ltd. | Nylon 66 | TUFNYL® |
| Lustran® ABS 308 | INEOS ABS (USA) | ABS | Lustran® ABS |