TAISOX 8003H
| Category: | HDPE , High Density Polyethylene |
| Manufacturer: | Formosa Plastics Corporation |
| Trademark: | TAISOX |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Bql4Y5_TAISOX-8003H.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
TAISOX 8003H is a high density polyethylene material,. This product is available in North America, Europe or Asia Pacific region. The processing method is blow molding. The main features of TAISOX 8003H are:
Typical application areas include:
|
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.958 | g/cm³ | ASTM D1505 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 0.30 | g/10 min | ASTM D1238 |
| Environmental Stress-Cracking Resistance | 30.0 | hr | ASTM D1693 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D) | 69 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | ASTM D638 | ||
| Yield | 30.4 | MPa | ASTM D638 |
| Fracture | 37.3 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 1000 | % | ASTM D638 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Impact Strength | 343 | kJ/m² | ASTM D1822 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Brittleness Temperature | -70.0 | °C | ASTM D746 |
| Vicat Softening Temperature | 127 | °C | ASTM D1525 |
| Melting Temperature | 134 | °C |
| Additional Information |
|---|
| Notched Izod Impact Strength, ASTM D256: 40 kg-cm/cm²Die Swell Ratio, FPC Method: 1.48Pich-off thickness, FPC Method: Good |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Processing (Melt) Temp | 160 - 180 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Mapex AT0320GN | Ginar Technology Co., LTD. | Nylon 66 | Mapex |
| SLOVALEN® PC 78 FRD 1 | Plastcom | PP, Unspecified | SLOVALEN® |
| WACKER SilGel® 611 A/B | Wacker Chemie AG | Silicone | WACKER SilGel® |
| XYRON™ X351V | Asahi Kasei Chemicals Corporation | PPE+PS | XYRON™ |
| Generic PP, Unspecified - Calcium Carbonate | Generic | PP, Unspecified | Generic |